2) glass fiber reinforced polymer concrete
玻璃纤维增强聚合物混凝土
1.
Orthogonal tests were carried out to prepare glass fiber reinforced polymer concrete with different proportions.
采用玻璃纤维来增强聚合物混凝土(PC),并通过一组正交试验测定了不同配比玻璃纤维增强聚合物混凝土(GFRPC)试样的抗压强度,分析了各试验因素对材料抗压强度的影响规律。
3) steel fiber reinforced and polymer modified concrete
钢纤维增强聚合物改性混凝土
1.
Impact tests of a new kind of pavement material for concrete bridge deck,steel fiber reinforced and polymer modified concrete(SFRPMC),were carried out by using a large cross-section SHPB system.
利用大尺寸Hopkinson压杆对新型混凝土桥面铺装材料——钢纤维增强聚合物改性混凝土(steel fiber reinforced and polymer modified concrete,SFRPMC)进行了冲击实验,并且在相同基准配合比下,与普通混凝土、钢纤维混凝土的冲击性能进行了对比。
4) SFRPMC
钢纤维增强聚合物改性混凝土(SFRPMC)
6) glass fibre reinforced concrete
玻璃纤维混凝土
1.
Through mechanical tests,some mechanical properties of glass fibre reinforced concrete of different fibre content,such as compressive strength,tensile strength,elastic modulus,and Poisson\'s ratio were studied,and other factors influencing the mechanical properties were put forward,which provided the experimental results for reference for the wide use of this new material.
通过力学试验,研究不同纤维掺量的玻璃纤维混凝土的抗压强度、抗拉强度、弹性模量、泊松比等力学性能,并提出了玻璃纤维混凝土力学性能的其他影响因素,为玻璃纤维混凝土这种新型材料的推广使用提供了可供参考的实验结果。
补充资料：玻璃纤维增强液晶聚合物
分子式：
CAS号：
性质：由玻璃纤维和液晶聚合物通过螺杆挤出机熔融共混挤出形成的材料。由于液晶聚合物在微小的外力作用下极容易取向，使成品力学性能呈显著的各向异性，制品接缝强度低，应用领域受到极大的限制。经玻璃纤维增强后，不仅克服上述缺点，降低了成本，而且拉伸强度由116MPa提高到137.3MPa，拉伸模量由9.6GPa提高到15.9GPa，使用温度也有所提高。已成为液晶聚合物的主流商品，在航空、电子、电器等领域中具有广泛的用途。
CAS号：
性质：由玻璃纤维和液晶聚合物通过螺杆挤出机熔融共混挤出形成的材料。由于液晶聚合物在微小的外力作用下极容易取向，使成品力学性能呈显著的各向异性，制品接缝强度低，应用领域受到极大的限制。经玻璃纤维增强后，不仅克服上述缺点，降低了成本，而且拉伸强度由116MPa提高到137.3MPa，拉伸模量由9.6GPa提高到15.9GPa，使用温度也有所提高。已成为液晶聚合物的主流商品，在航空、电子、电器等领域中具有广泛的用途。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条