1) alumina granule
颗粒状氧化铝
2) alumina particle
氧化铝颗粒
1.
That alumina particle was modified with silane coupling agent was discussed,and a condition that the alumina dispersion had thixotropic property was found in to increase surface quality and wet intensity of coating layer,improve the capacity of absorb ink,and decrease the cost of coating layer.
本文用硅烷偶联剂对氧化铝颗粒进行了改性研究,找到了使氧化铝分散液产生触变特性的条件,不但提高了产品的表观质量和涂层的湿膜强度,增大了涂层的吸墨量,还大幅度降低了成本。
2.
The heatresistant steel (HRS) matrix composites reinforced by alumina particles coated with Ni and TiN respectively by means of chemical vapor deposition method are fabricated.
通过化学气相沉积方法在氧化铝颗粒表面分别获得了Ni、TiN涂层。
3.
Chemical vapor deposition is used for coating the surface of alumina particle, and alumina particle/heat resistant steel composites are manufactured by the vacuum infiltration technique.
采用化学气相沉积技术对氧化铝颗粒表面进行涂层处理,通过负压铸渗工艺制备了氧化铝颗粒耐热钢基复合材料,并对其在900℃下的高温磨料磨损特性进行了研究,结果表明:耐热钢在高温下的磨损主要是由磨料的滚压形成的挤出唇、翻边脱落所引起,磨损量较大,而复合材料高温磨损时颗粒突出于基体,承受载荷多,阻碍了磨粒对基体的损伤,因而抗磨性较好,其高温耐磨性是基体材料的33倍多。
3) Al_2O_3·3H_2O
水合氧化铝颗粒
4) alumina pellet
片粒状氧化铝
5) alumina particle reinforcement
氧化铝颗粒增强体
6) platelet Al_2O_3 grain
板片状氧化铝晶粒
补充资料：氧化铝颗粒增强体
分子式：
CAS号：
性质：通常由于加入到金属基中。譬如：在Al合金中加入体积分数为30％，粒径为0.3μm的Al2O3颗粒，使材料在300℃时的拉伸强度仍达到220MPa，并且所加入氧化铝颗粒，还可促进致密化，而合金的电导率并不降低。目前，氧化铝颗粒增强铝、镁或钛合金正用于制备内燃机引擎。氧化铝颗粒也被加入到Ni-AlIC-221，制成金属间化合物基复合材料(IMCS)。氧化铝颗粒与基体具有很好的化学相容性，几乎不发生界面化学反应。这种复合材料的弹性模量比基体材料或普通Ni基合金要高出20％～30％。
CAS号：
性质：通常由于加入到金属基中。譬如：在Al合金中加入体积分数为30％，粒径为0.3μm的Al2O3颗粒，使材料在300℃时的拉伸强度仍达到220MPa，并且所加入氧化铝颗粒，还可促进致密化，而合金的电导率并不降低。目前，氧化铝颗粒增强铝、镁或钛合金正用于制备内燃机引擎。氧化铝颗粒也被加入到Ni-AlIC-221，制成金属间化合物基复合材料(IMCS)。氧化铝颗粒与基体具有很好的化学相容性，几乎不发生界面化学反应。这种复合材料的弹性模量比基体材料或普通Ni基合金要高出20％～30％。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。