1) barium-sodium niobate
铌酸钠钡
2) barium sodium niobate
铌酸钡钠
1.
This paper reports that the barium sodium niobate (BNN) optical-waveguide film with orientation [110] has been epitaxially grown on the (100) plane of substrate KTiOPO4(KTP) by pulsed laser deposition (PLD).
报道了用脉冲激光淀积（ＰＬＤ）方法在磷酸氧钛钾（ＫＴＰ）晶体（１００）面上生长沿［１１０］取向的铌酸钡钠（ＢＮＮ）光波导薄膜。
3) (Sr,Ca)_2NaNb_5O_(15)
铌酸锶钡钠
4) KNSBN
钾钠铌酸锶钡
1.
OPTICAL PROPERTIES IN KNSBN CRYSTAL MATERIALS;
双掺钾钠铌酸锶钡晶体光学特性研究
2.
9,KNSBN) thin films with stoichiometric proportions have been successfully grown on MgO(001) substrate by the sol_gel process.
采用溶胶_凝胶法在氧化镁单晶衬底上制备了符合化学计量比的完全填充型铁电钾钠铌酸锶钡(KNSBN)薄膜,通过X射线衍射,摇摆曲线,X射线Φ扫描,扫描电子显微镜等方法研究了薄膜的微结构,采用Adachi法研究了薄膜的电光特性。
3.
grown and prepared KNSBN crystal samples with different V concentrations in our experiment.
成功地生长、制备出了一系列合不同掺钒浓度的钾钠铌酸锶钡（ＫＮＳＢＮ：Ｖ）晶体样品。
5) BNN
铌酸钡钠晶体
6) sodium-barium niobate ceramics
铌酸钡钠陶瓷
补充资料：铌酸钠
分子式：NaNbO3
CAS号：
性质：无色三斜晶体（室温晶格常数a=556.8pm,b=550.5pm,c=1551.8pm）。随着温度的降低，铌酸钠有5种晶型转变：非极性的α相在604℃转变为β相（立方晶系钙钛矿结构），562℃转变为γ相（假四方晶系，非极性），354℃转变为δ相（菱形晶系，具有反铁电性，介电常数达到最大值1800，密度7.127 g/cm3），200℃时变为ε相（单斜晶，具有铁电性质）。铌酸钠属反铁电陶瓷，点群222，居里点480℃。以氧化铌和碳酸钠为原料用热压烧结制备。主要应用于两个方面：一是利用反铁电-铁电相变时的双电滞回线，作贮能容器、压电调节元件：二是利用反铁电-铁电相变的体积效应，用作换能器。
CAS号：
性质：无色三斜晶体（室温晶格常数a=556.8pm,b=550.5pm,c=1551.8pm）。随着温度的降低，铌酸钠有5种晶型转变：非极性的α相在604℃转变为β相（立方晶系钙钛矿结构），562℃转变为γ相（假四方晶系，非极性），354℃转变为δ相（菱形晶系，具有反铁电性，介电常数达到最大值1800，密度7.127 g/cm3），200℃时变为ε相（单斜晶，具有铁电性质）。铌酸钠属反铁电陶瓷，点群222，居里点480℃。以氧化铌和碳酸钠为原料用热压烧结制备。主要应用于两个方面：一是利用反铁电-铁电相变时的双电滞回线，作贮能容器、压电调节元件：二是利用反铁电-铁电相变的体积效应，用作换能器。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。