1) triacetate spun yarn
三醋酸纤维细纱
2) acetate yarn
醋酸纤维纱
4) cellulose triacetate
三醋酸纤维素
1.
The structure and properties of cellulose triacetate acetylation were determined by IR,1H-NMR,XRD,DSC and chemical analysis.
采用乙酸酐/乙酸/硫酸体系制备了三醋酸纤维素(CTA),运用IR,化学滴定,1H-NMR,X射线衍射,DSC等手段对产物的结构及性质进行了表征和测试。
2.
The factors,including triphenyl phosphate(TPP) content,hydrolization time,the volume of water and catalyzer concentration,affecting degree of substitution(DS) of cellulose triacetate(CTA) in hydrolization are studied.
研究了增塑剂磷酸三苯酯(TPP)含量、含水量、催化剂的比例以及水解时间对三醋酸纤维素(CTA)水解产物取代度(DS)的影响。
3.
With cellulose triacetate (CTA) as membrane material, thiophen sulfone as solvent, and polyethyleneglycol(PEG) with proper amount of other additives as multi-element pore-forming agent, a high performance hollow fiber nanofiltration (NF) membrane is prepared by gel-freezing method.
采用三醋酸纤维素 (CTA)为膜材料 ,环丁砜作溶剂 ,以聚乙二醇 (PEG)为主、加入适量其它添加剂组合成多元型致孔剂 ,通过冻胶法纺丝 ,制得中空纤维纳滤 (NF)膜 。
5) three cellulose acetate membrane
三醋酸纤维素膜
1.
The measure of copper and iron content in three cellulose acetate membrane of the zinc-silver battery by using the AIR- C2H2 flame atomic- absorption spectroscopy and make synthetically consideration of the measuring conditions and factors were atuded.
运用空气-乙炔火焰原子吸收光谱法同时测定银锌电池三醋酸纤维素膜中铜铁含量,并对测定条件和干扰因素进行了综合分析 该测定方法具有很好的灵敏度,干扰少,选择性和重现性好等优点 测定样品铜铁含量的相对标准偏差均小于1。
6) cellulose triacetate
纤维素三醋酸酯
1.
The cellulose triacetate (CTA) prepared by heterogeneous acetylation and coated on small pore 3 aminopropyl silica gel (10nm) was used as chiral stationary phase for HPLC (OA column).
合成了纤维素三醋酸酯，并被涂于小孔硅胶上制备成ＨＰＬＣ手性固定相。
补充资料：三醋酸纤维
分子式：
CAS号：
性质：俗称三醋酸纤维，是纤维素酯纤维的一种。指从棉短绒、木材等植物材料中提取和纯化得到的纤维素为原料，与醋酸酐反应生成含结合醋酸量达61.5%～62.5%的三醋酸纤维素后，用二氯甲烷溶解后经纺丝所制得的纤维。该纤维具有较好的耐光性；经受热处理时能诱导结晶，故能提高该纤维制品的尺寸稳定性。纤维相对密度1.30，干态强度1.0～1.2cN/dtex，伸长率25%～35%，公定吸湿率3.5%，干湿态强度比67%～72%。产品形式主要为短纤维，用于制作仿毛织物和制品。
CAS号：
性质：俗称三醋酸纤维，是纤维素酯纤维的一种。指从棉短绒、木材等植物材料中提取和纯化得到的纤维素为原料，与醋酸酐反应生成含结合醋酸量达61.5%～62.5%的三醋酸纤维素后，用二氯甲烷溶解后经纺丝所制得的纤维。该纤维具有较好的耐光性；经受热处理时能诱导结晶，故能提高该纤维制品的尺寸稳定性。纤维相对密度1.30，干态强度1.0～1.2cN/dtex，伸长率25%～35%，公定吸湿率3.5%，干湿态强度比67%～72%。产品形式主要为短纤维，用于制作仿毛织物和制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。