1) poly-m-methyl styrene
聚间甲基苯乙烯
2) syndiotactic poly(p-methylstyrene)
间规聚对甲基苯乙烯
3) styrene/p-methylstyrene syndiotactic copolymer
苯乙烯与对甲基苯乙烯的间规共聚物
4) Chloromethylated polystyrene
氯甲基聚苯乙烯
1.
Chloromethylated polystyrene was transformed into aminomethylated polystyrene via Gabriel reaction using potassium salt of phthalic imidine as the reagent of nucleophilic substitution.
以邻苯二甲酰亚胺钾盐为亲核取代试剂,采用相转移催化体系通过Gabriel反应,将氯甲基聚苯乙烯转变为苯二甲酰亚胺基甲基聚苯乙烯,考察了各种因素对相转移催化反应的影响规律,探讨了相转移催化机理。
2.
Aminomethyl polystyrene(AMPS) was prepared from chloromethylated polystyrene(CMPS) via Gabriel reaction by means of phase-transfer catalysis using potassium phthalic imidine as a nucleophilic substitution reagent.
以邻苯二甲酰亚胺钾盐为亲核取代试剂,通过Gabriel反应,借助相转移催化剂实现了氯甲基聚苯乙烯(CMPS)转变为氨甲基聚苯乙烯(AMPS)的高分子功能化反应,转化率达85%。
5) poly(α-methylstyrene)
聚甲基苯乙烯
1.
the degree of polymerization x for poly(α-methylstyrene)chain with two-side side group is calculated, which agrees with the experiment data.
在旋转异构态理论基础上,建立双侧基高分子链均方旋转半径的计算公式,由此得到聚甲基苯乙烯的均方旋转半径特征比与链长的关系,计算结果与实验数值十分一致。
6) Pα-MS
聚α-甲基苯乙烯
补充资料：聚对甲基苯乙烯
分子式：
CAS号：
性质： 为对甲基苯乙烯均聚物。各种性能类同聚苯乙烯，并保持良好的成型加工性，耐热性提高并可交联。拉伸强度48MPa，弹性模量2210MPa，悬臂梁缺口冲击强度16J/m，热变形温度95℃。对甲基苯乙烯进行悬浮聚合制得。主要用于代替聚苯乙烯在需耐温较高场合用作电器配件和包装，并用于照明器材等。
CAS号：
性质： 为对甲基苯乙烯均聚物。各种性能类同聚苯乙烯，并保持良好的成型加工性，耐热性提高并可交联。拉伸强度48MPa，弹性模量2210MPa，悬臂梁缺口冲击强度16J/m，热变形温度95℃。对甲基苯乙烯进行悬浮聚合制得。主要用于代替聚苯乙烯在需耐温较高场合用作电器配件和包装，并用于照明器材等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。