1) elongation at rupture
断裂延伸率;断裂伸
3) extension fracture
延伸断裂
4) long time rupture elongation
持久断裂延伸率
5) zero elongation rupture
零延伸断裂
1.
Technique used to prevent zero elongation rupture of SBS waterproofing membrane;
防止SBS防水卷材零延伸断裂的施工技术
6) elongation at break
断裂伸长率
1.
The tensile strength,elongation at break,notch impact strength and flexural strength of PBT were increased by 12%,100%,1.
1份时,PBT的拉伸强度提高12%,断裂伸长率提高100%,冲击强度提高10%,弯曲强度提高5%,综合力学性能最好。
2.
The tensile strength and the elongation at break were 23 MPa and 460% when the compound plasticizing agent were made up of(1.
在此条件下,PVA217流延膜的各种性能较好,拉伸强度约为23 MPa,断裂伸长率约为460%。
3.
The resin could be cured at ambient temperature and the tensile strength and elongation at break of the cured resin were 20 MPa and 106% respectively,which could be used to make high flexible products or could be also added in normal unsaturated polyester resins to improve their anti-impact properties and elongation at break.
介绍了1种新型二异氰酸酯改性不饱和聚酯,该树脂可以室温固化,固化后树脂的拉伸强度和断裂伸长率分别可达20 MPa和106%。
补充资料：多肽链延伸因子
多肽链延伸因子
多肽链延伸因子 polypeptide chain elonga－tion factor
蛋白质生物合成中参与多肽链延伸过程的蛋白质因子。从大肠杆菌等原核细胞可纯化获得三种延伸因子（elongation factor），即eftu，efts和efg，分子量大约分别为4.7万，3.6万和8.3万。eftu与gtp结合成eftu-gtp，然后再与氨酰trna结合，形成三复合体（ternary complex）氨酰-trna-eftu－gtp。这种三复合体与核糖体的氨酰trna部位（a部位，aminoacyl site）结合，继而gtp被分解，eftu以eftu－gtp的形式从核糖体上游离出来。游离的eftu－gdp与efts反应，再生成eftu－ts，然后与gtp结合成eftu－gtp。另一方面结合在p部位（peptide transfer）。多肽链即可延长一个氨基酸残基。接着肽基trna从a部位转移（translccation）到p部位，p部位的trna从核糖体上脱离下来。该反应由efg（g因子，亦称为移位酶）催化，再将一分子的gtp水解。如图所示，由于上述反应的逐次反复进行，而使多肽链延伸反应得以进行，每延长一个氨基酸残基，就水解两分子gtp。动物细胞或其他真核细胞基本上也以同样机制进行多肽链的延伸，并且也分离到了对应于原核细胞的各因子。