您的位置:首页 -> 词典 -> 铁锰铜合金
1)  ferromanganin
铁锰铜合金
2)  Mn-Cu alloy
锰铜合金
1.
The dynamics characters of axis sleeve made of the new Mn-Cu alloy is investigated, which is used as absorber in the high-speed rotary fusee-testing machine.
根据基础激振—共振质量法测试原理设计专用的实验测试系统,对作为高速旋转引信实验机减振部件使用的新型锰铜合金圆环类部件进行动力学特性测试。
2.
Variance of phyxics and mechanical property of Steel and Mn-Cu alloy are enormous, obtain good joint is difficult by conventional welding method.
钢与ZMnD-1J锰铜合金在物理、力学性能方面差异巨大,用传统的方法焊接,难以得到性能良好的接头。
3)  Cr-Mn-Cu alloy white cast iron
铬锰铜合金白口铸铁
1.
The wear resistance of Cr-Mn-Cu alloy white cast iron after heat treatment was studied and compared with that of as-cast Cr-Mn-Cu alloy white cast iron,the wear failure mechanism and microstructure on the wear end surface and nonwear end surface were analyzed.
以铬锰铜合金白口铸铁的铸态材料为对比材料,考察了热处理后的铬锰铜合金白口铸铁材料的耐磨性能,对试验材料的磨损失效机理和磨损端面与无磨损端面的金相组织进行了分析。
2.
The wearing resistance,microstructure,worn surface morphology and hardness change in wearing end-face and non-wearing end-face of Cr-Mn-Cu alloy white cast iron were tested and analyzed.
对铬锰铜合金白口铸铁的耐磨性、无磨损端面及磨损端面的微观组织、磨损形貌及硬度进行了试验和分析。
3.
The erosive-wear resistance of heat treated Cr-Mn-Cu alloy white cast iron was investigated compared with that of as-cast one, and the impact fractures,the erosive-wear resistant failure mechanism and the section metallurgical structure of the test materials were analyzed.
以铸态铬锰铜合金白口铸铁为对比材料,考察了热处理后的铬锰铜合金白口铸铁的抗冲蚀磨损性能,并对试验材料的冲击断口形貌、抗冲蚀磨损失效机理和冲蚀磨损横切面的金相组织进行了分析。
4)  zircal
锌镁铜铬锰铁硅合金
5)  Fe-Mn alloy
锰铁合金
1.
Possibility of oxidizing dephosphorization for Fe-Mn alloys is discussed on the basis of thermodynamic analysis and the previous experimental data.
通过热力学分析和已有的实验结果说明了锰铁合金氧化脱磷的可能性。
6)  Manganin ['mæŋɡənin]
锰铜,锰镍铜合金,锰铜线;锰铜电阻合金
补充资料:低锗锰铜合金
分子式:
CAS号:

性质: 含锗较低的锗锰铜合金。成分为锗0.5%~2%,锰8%~10%,其他20%,铜余量。电阻率35×10-8Ω·m。平均电阻温度系数±3×10-6℃-1(20℃)。平均对铜热电动势≤1.0μV/℃。密度8.6g/cm3。熔点920℃。抗拉强度392~441MPa。延伸率2%。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。