2) initial pitting
初始点蚀
3) initial cavitation
初始汽蚀
4) initial corrosion
初期腐蚀
1.
Influence of Cl~- concentration on the initial corrosion behavior of 2A12 aluminum alloy
Cl~-含量对2A12铝合金初期腐蚀行为的影响
2.
With measuring and analyzing corrosion morphology,potential and EIS,the initial corrosion of aluminum alloys in marine atmosphere and correlation of simulated marine atmosphere accelerated corrosion test and outfield corrosion test were studied.
通过对模拟海洋大气加速腐蚀试验和外场暴露试验中的LY12铝合金初期腐蚀形貌、电位和交流阻抗等的测量和分析,研究铝合金在海洋大气环境下的初期腐蚀行为,并考察加速腐蚀试验结果和外场暴露试验结果的相关性。
3.
Series of accelerated corrosion tests were conducted in simulated marine atmosphere to study initial corrosion of LY12 aluminum alloy(corresponds to USA 2024) at different humidity.
根据表面带Cl-的LY12铝合金在模拟海洋大气环境中的腐蚀形貌、增重、最大点蚀深度以及腐蚀体系的自腐蚀电位、交流阻抗等变化,分析相对湿度对其初期腐蚀行为的影响。
5) initial atmospheric corrosion
初期大气腐蚀
1.
The influence of NaCl and lower concentration of SO2 on the initial atmospheric corrosion of A3 steel at 25℃and 80% relative humidity (RH) was investigated.
研究了在25℃、相对湿度为80％的条件下,NaCl和低浓度 SO2的协同效应对A3钢初期大气腐蚀行为的影响。
2.
The influence of temperature on initial atmospheric corrosion behavior of AZ91D magnesium alloy was studied by optical microscopy(OM),scanning electron microscopy(SEM),energy dispersion spectrum(EDS)and X-ray diffraction(XRD).
采用金相显微镜、扫描电镜(SEM)、能谱仪(EDS)、X-射线衍射(XRD)研究温度对AZ91D镁合金初期大气腐蚀的影响,并且分析了AZ91D镁合金在不同温度的大气环境中的腐蚀形貌和腐蚀产物。
6) initial corrosion mechanism
初期腐蚀机理
补充资料：点蚀系数
分子式：
CAS号：
性质：腐蚀挂片上发生点蚀的最大深度与按重量损失计算出的平均腐蚀深度之比值。
CAS号：
性质：腐蚀挂片上发生点蚀的最大深度与按重量损失计算出的平均腐蚀深度之比值。