1) Yellow iron oxides
黄氧化铁
2) iron oxide yellow
氧化铁黄
1.
Process of preparing α-FeOOH nanorods with air oxidation is divided into two steps,preparation of crystal seeds and production of iron oxide yellow particles.
此法可制得黄色,棒状,长、径分别约为300nm、50nm的纳米氧化铁黄粉末。
2.
Nano-sized iron oxide yellow particles were prepared by air oxidation,and characterized by XRD and TEM.
采用空气氧化法制备了纳米级氧化铁黄颗粒,并用XRD、TEM对样品进行了表征。
3.
Nanosized iron oxide yellow particles were prepared by oxidizing ferrous sulfate using sodium chlorate.
利用氯酸钠氧化硫酸亚铁工艺制备纳米氧化铁黄 ,采用 TG- DTA、XRD、TEM等手段对样品形态结构进行表征 。
3) yellow iron oxide
氧化铁黄
1.
A process of producing yellow iron oxide pigment by ferrous saltof by-product is deseribed.
从分析我国氧化铁黄生产及市场现状出发，试验选择了以钛白粉厂副产硫酸亚铁为原料，通过原料纯化、分步中和、分步控制氧化的常温合成工艺路线。
5) yellow iron oxide
黄色氧化铁
6) transparent yellow iron oxide
透明氧化铁黄
1.
Process control by various additives-dosage during and/or after reaction can result in transparent yellow iron oxide characterized by high-clarity, good dispersibility, pure color phase and excellent heat resistance.
介绍了透明氧化铁黄颜料的性质、用途、制备方法以及改性处理。
补充资料：氧化铁黄
分子式：
CAS号：
性质：又称铁黄。以α-水合三氧化二铁为主要成分的黄色无机颜料，其化学式为α-Fe2O3·H2O，或者为α-FeOOH。外观为黄色，粒子呈针状。粒度为0.2～1.5μm。表面积为7～15m2/g。密度为4.03g/cm3。折射率2.3。吸油量为36～55g/100g。氧化铁黄主要是采用硫酸亚铁氧化法生产，可直接用硫酸亚铁溶液，也可用铁屑与硫酸制备硫酸亚铁，再加入苛性钠溶液和空气制得晶种、晶种成长、加热氧化、过滤、洗涤、干燥并粉碎而成，也可采用苯胺法生产。主要用于涂料、建筑材料、橡胶等作着色颜料，也用作其他氧化铁的中间体如氧化铁红、铁黑等。
CAS号：
性质：又称铁黄。以α-水合三氧化二铁为主要成分的黄色无机颜料，其化学式为α-Fe2O3·H2O，或者为α-FeOOH。外观为黄色，粒子呈针状。粒度为0.2～1.5μm。表面积为7～15m2/g。密度为4.03g/cm3。折射率2.3。吸油量为36～55g/100g。氧化铁黄主要是采用硫酸亚铁氧化法生产，可直接用硫酸亚铁溶液，也可用铁屑与硫酸制备硫酸亚铁，再加入苛性钠溶液和空气制得晶种、晶种成长、加热氧化、过滤、洗涤、干燥并粉碎而成，也可采用苯胺法生产。主要用于涂料、建筑材料、橡胶等作着色颜料，也用作其他氧化铁的中间体如氧化铁红、铁黑等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。