说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 玻璃纤维,玻璃丝
1)  fibreglass [英]['faɪbəɡlɑ:s]  [美]['faɪbɚ'glæs]
玻璃纤维,玻璃丝
2)  spun glass
玻璃丝,玻璃纤维
3)  glass fibre
玻璃纤维、玻璃丝
4)  stiff glass-fiber
废玻璃纤维硬丝
1.
Foam glass was prepared with sintered process, using moderate amount of additives and the powder of stiff glass-fiber as main material.
以废玻璃纤维硬丝为主要原料 ,添加适量外加剂 ,采用烧结法制备出质量符合要求的泡沫玻璃。
5)  stiff glass fiber
玻璃纤维硬丝
1.
Foam glass was prepared with sintered process, using moderate amount of additives and the powder of waste stiff glass fiber as main material and its foaming mechanism was investigated.
以废玻璃纤维硬丝为主要原料 ,添加适量外加剂 ,采用烧结法制备出质量符合要求的泡沫玻璃 ,并探讨了其发泡机理 。
6)  glass fiber tow
玻璃纤维丝束
1.
For better estimation of GFRP properties,the authors made some experimental studies about tensile properties of glass fiber tow according to corresponding Chinese national test standards.
为便于玻璃纤维增强塑料性能估算的实际应用,在相关国家测试标准的基础上,我们对玻璃纤维丝束的拉伸性能做了些对比试验研究。
补充资料:玻璃纤维
玻璃纤维
glass fibre

   由玻璃制成的无机纤维。成分为二氧化硅、氧化铝、氧化钙、氧化硼、氧化镁、氧化钠等。根据玻璃中碱含量的多少,分为无碱玻璃纤维(氧化钠 0 ~ 2%,属铝硼硅酸盐玻璃)、中碱玻璃纤维(氧化钠 8%~12%,属含硼或不含硼的钠钙硅酸盐玻璃)和高碱玻璃纤维(氧化钠13%以上,属钠钙硅酸盐玻璃)。玻璃纤维比有机纤维耐高温,不燃,抗腐蚀,隔热、隔声性能好,抗拉强度高,电绝缘性能好。但性脆,耐磨性较差。
    生产玻璃纤维的主要原料是石英砂 、氧化铝和叶蜡石、石灰石、白云石、硼酸、纯碱、芒硝、萤石等。生产方法分为两类,一类是将熔融玻璃直接制成纤维;另一类是将熔融玻璃先制成直径20毫米的玻璃球或棒,再以多种方式加热重熔后制成直径3~8微米的纤维。通过铂合金板以机械拉丝方法拉制的无限长玻璃纤维,称为连续玻璃纤维,通称长纤维。通过辊筒或气流制成的非连续玻璃纤维,称为定长玻璃纤维,通称短纤维。借离心力或高速气流制成的细、短、絮状玻璃纤维,称为玻璃棉。玻璃纤维经加工,可制成多种形态的制品 ,如纱 、无捻粗纱、短切原丝、布、带、毡、板、管等。
    玻璃纤维按组成、性质和用途分为不同级别。E 级玻璃纤维使用最普遍 ,广泛用作电绝缘材料 ;S 级为特殊纤维,具有超高强度,主要用于军事方面;C级比E级更具有耐化学腐蚀性,用作电池隔离板、化学滤毒器;A 级为碱性玻璃纤维,多用作复合材料的增强材料。