1) cold melt
低温熔化
2) lowest melting temperat ure
最低熔化温度
3) low temperature frit
低温熔块
1.
The influences of lithia content on the melting temperature,mechanical properties and thermal expansion coefficient of low temperature frit were studied.
本文研究了氧化锂加入量对低温熔块的熔融温度、力学性能、热膨胀系数的影响。
4) low temperature molten salts
低温熔盐
1.
In order to increase the bonding strength of hydroxyapatite (HA) coating on a steel substrate, Al-Ti/HA composite coatings were successfully prepared in AlCl_3-NaCl-TiCl_3 low temperature molten salts incorporated with HA particles.
为了提高羟基磷灰石涂层的结合强度,在AlCl3 NaCl-TiCl3低温熔盐体系中加入HA微粒,复合电沉积制备Al-Ti/HA复合涂层,并对涂层的表面形貌、结构和结合强度进行了研究。
5) low temperature melt
低温熔体
1.
The effect of high density pulse electric current (HDPEC) on the solidification structure of the low temperature melt(LTM) of commercial A356 aluminum alloy was investigated.
研究了高密度脉冲电流对A356铝合金低温熔体凝固组织的影响,实验中对680和630℃的低温熔体施加脉冲电流处理,对比试验和凝固曲线侧试结果表明。
补充资料：最低临界溶解温度
分子式：
CAS号：
性质：又称为最低临界溶解温度，最低会溶温度(1ower consolute temperature)。形成部分互溶物系的两种液体，随着温度的降低，二液体的相互溶解度增加。互相平衡的二液相的组成逐渐接近，当降低至某一温度时，二液相组成相同，二液相间的界面消失，在该温度以下，只有一个均匀液相。
CAS号：
性质：又称为最低临界溶解温度，最低会溶温度(1ower consolute temperature)。形成部分互溶物系的两种液体，随着温度的降低，二液体的相互溶解度增加。互相平衡的二液相的组成逐渐接近，当降低至某一温度时，二液相组成相同，二液相间的界面消失，在该温度以下，只有一个均匀液相。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条