1) glass silicide coating
玻璃硅化物涂层
2) silica glass layer
氧化硅玻璃层
3) glass coating
玻璃涂层
1.
The effects of processing parameters and adding rare earth on the corrosion resistance of glass coatings on metal surface were studied by means of electrochemical test, immersion test,pitting test and scanning electron microscope.
利用斑点试验、点蚀试验、电化学测试及扫描电镜等方法 ,研究了熔敷温度、保温时间和稀土添加量等工艺参数对热熔敷法制备的玻璃涂层耐蚀性的影响 ,探讨了添加稀土提高玻璃涂层耐蚀性的机理。
2.
The corrosion mechanism of flame sprayed glass coatings was studied in this paper.
研究了手工火焰喷涂玻璃涂层的腐蚀破坏机理。
3.
The impact test, the thermal shock test and the scanning electron microscopy were used to investigate the effect of rare earth oxide on the adhesiveness between the glass coating and the base metal.
利用冲击试验、热震试验和扫描电镜等方法研究了添加氧化铈对玻璃涂层与金属基体密着性的影响规律。
4) silicide coating
硅化物涂层
1.
Microstructure and formation mechanism of silicide coating prepared by pack cementation;
包渗法制备硅化物涂层的结构形貌及形成机理
2.
The silicide coatings on C103 niobium alloy were prepared by complex packing cementation.
采用复合包渗法在C103铌合金基体上制备硅化物涂层,进行1500℃静态氧化实验,室温～1500℃热震实验,利用X射线衍射(XRD)、扫描电镜(SEM)、能谱分析(EDS)等检测手段对涂层氧化前后的组织结构进行观察,分析涂层形成机理、硅化时间对涂层组织结构的影响以及涂层氧化前后组织形貌的变化。
5) TiO 2 coated glass
TiO2涂层玻璃
6) glass-based coating
玻璃基涂层
1.
To solve the severe oxidation problems of molybdenum at high temperature in air,a glass-based coating has been successfully developed to protect molybdenum electrodes from oxidation in the process of heating up kiln.
针对钼在高温下极易氧化的问题,开发了一种在烤窑时防止钼电极被氧化的玻璃基涂层。
补充资料：一氧化硅
化学式 SiO。白色立方晶体；熔点＞1702°C，沸点1880°C，密度2.13克/厘米3。一氧化硅不太稳定，在空气中会氧化成二氧化硅；易溶于强碱溶液，生成硅酸盐并放出氢气。当一氧化硅蒸气缓慢冷凝时会歧化（见歧化反应）而成硅和二氧化硅。一氧化硅能溶于氢氟酸和硝酸的混合酸中并放出四氟化硅。一氧化硅可由二氧化硅在高温下与单质硅作用后迅速冷却制得：
固态一氧化硅可作绝缘材料。
固态一氧化硅可作绝缘材料。