1) epoxy-cement mortar
环氧水泥砂浆
2) epoxy latex cement mortar
环氧乳液水泥砂浆
3) epoxy grout(mortar)
环氧胶泥(砂浆)
4) mortar
[英]['mɔ:tə(r)] [美]['mɔrtɚ]
水泥砂浆
1.
Mechanical and abrasion properties of fiber reinforced rubberized mortar;
纤维增强橡胶粉水泥砂浆的力学性能和耐磨性能研究
2.
A study on the cylinder-mould testing method for the compressive strength of the mortar with highly fine-grained sand;
筒压法检测特细砂水泥砂浆抗压强度的试验研究
3.
The structural and electric properties of carbon fiber reinforced mortar and the related factors;
碳纤维水泥砂浆的力学与电性能及其影响因素研究
5) cement mortar
水泥砂浆
1.
Research on the influence of property of composite cement mortar to silane coupling agents;
硅烷偶联剂对复合水泥砂浆性能的影响
2.
Study on the properties of water-based epoxy resin modified cement mortar;
水性环氧树脂改性水泥砂浆性能的研究
3.
Synthesis and effect on cement mortar of HBS lignin base epoxy resin;
高沸醇木质素环氢树脂-水泥砂浆复合材料的研制
6) cement grout
水泥砂浆
1.
The comparative experiment researches the main property of normal cement grout and polyurethane cement grout.
在现有材料基础上通过对比试验选定了一种新型无溶剂聚氨酯材料作为水泥改性剂,对比试验研究了普通水泥砂浆和聚氨酯水泥砂浆的主要性能,研究表明:采用相同水灰比,聚氨酯水泥砂浆与普通水泥砂浆相比,抗折、抗压强度降低,但抗渗性能和抗冻性能显著提高,同时,抗碳化性能有一定改善。
2.
Based on the physical and chemical effects of surface energy,the research added an enhancing agent to increase the injection rate of cement grout.
在半柔性路面材料的应用中,发现水泥砂浆的灌入率不超过75%,说明多孔沥青混合料中还存在大量的空隙,这严重影响着半柔性材料的力学性能以及路用性能。
补充资料：1,4-双[(2,3-环氧丙氧基)甲基]环氧乙烷
CAS: 14228-73-0
分子式: C14H24O4
中文名称: 2,2'-[1,4-环己二基双(亚甲基氧亚甲基)]双-环氧乙烷；1,4-双[(2,3-环氧丙氧基)甲基]环氧乙烷；1,4-双[(缩水甘油氧)甲基]环己烷
英文名称: 2,2'-[1,4-cyclohexanediylbis(methylene oxymethylene)] bis-Oxirane
1,4-bis[(2,3-Epoxypropoxy)ethyl]cyclohexane
2,2'-[1,4-cyclohexanediylbis(methyleneoxymethylene)]bis-oxiran
分子式: C14H24O4
中文名称: 2,2'-[1,4-环己二基双(亚甲基氧亚甲基)]双-环氧乙烷；1,4-双[(2,3-环氧丙氧基)甲基]环氧乙烷；1,4-双[(缩水甘油氧)甲基]环己烷
英文名称: 2,2'-[1,4-cyclohexanediylbis(methylene oxymethylene)] bis-Oxirane
1,4-bis[(2,3-Epoxypropoxy)ethyl]cyclohexane
2,2'-[1,4-cyclohexanediylbis(methyleneoxymethylene)]bis-oxiran
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条