1) Microstructure of MgO-C brick
镁碳砖的显微结构
3) microstructure evolution
显微结构的演化
1.
The microstructure evolution of the polycrystalline solids is a complex procedure,which is a function of many factors.
多晶固体材料的显微结构的演化与诸多因素密切相关，是一复杂的过程。
5) MgO-C brick
镁碳砖
1.
TiC-C compound powder:syntiesis and its influence on oxidation resistance of low-carbon MgO-C bricks;
TiC-C复合粉体的制备及其对低碳镁碳砖抗氧化性能的影响
2.
Field experimental study on bonding between slag-splashed layer and MgO-C brick in a converter;
复吹转炉溅渣层与镁碳砖之间结合的现场试验研究
6) magnesia-carbon brick
镁碳砖
1.
Microstructure and mechanical behavior of magnesia-carbon brick bonded by catalytically activated resins;
催化活化树脂碳化后炭结构及其结合镁碳砖的力学行为
2.
The application of magnesia-carbon brick brasque in 5t arc furnace can effctively reduce stop time in hot furnace, protect furnace from troubles of furnace bottom inversion.
镁碳砖炉衬在５ｔ电弧炉上应用表明：该材料能有效地减少热停工时间，杜绝由于因镁砂、卤水打结、烧结不好的炉衬造成严重翻炉底等问题。
3.
Magnesia-carbon brick has high fireproof,thermal shock resistance,spalling resistance and slag resistance,which is used for the generalizing application in converter as furnace lining material.
镁碳砖具有高耐火性,良好的抗热震性、抗剥落、抗渣性。
补充资料：镁碳砖
分子式：
CAS号：
性质：以氧化镁和碳为主要成分的耐火制品。含氧化镁60%～90%，碳10%～40%。具有优良的抗渣侵蚀性、熔渣渗透性、热震稳定性和导热性。显气孔率为3%～10%。采用高纯镁砂粉粒、碳素材料（包括石墨）和焦油沥青或树脂等为原料，经配料、热混、成型后，再经300℃左右或1000℃以上焙烧而成。为抑制砖中的碳的氧化，常添加铝、硅、镁等金属或氮化硼，加入量不超过5%。主要用于炼钢氧化转炉的炉衬、出钢口，高功率电炉炉墙热点部位，以及炉外精炼炉内衬、盛钢桶渣线部位等。
CAS号：
性质：以氧化镁和碳为主要成分的耐火制品。含氧化镁60%～90%，碳10%～40%。具有优良的抗渣侵蚀性、熔渣渗透性、热震稳定性和导热性。显气孔率为3%～10%。采用高纯镁砂粉粒、碳素材料（包括石墨）和焦油沥青或树脂等为原料，经配料、热混、成型后，再经300℃左右或1000℃以上焙烧而成。为抑制砖中的碳的氧化，常添加铝、硅、镁等金属或氮化硼，加入量不超过5%。主要用于炼钢氧化转炉的炉衬、出钢口，高功率电炉炉墙热点部位，以及炉外精炼炉内衬、盛钢桶渣线部位等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。