1) TiO_2 anatase (101) surface
锐钛矿相TiO_2(101)表面
2) TiO2 anatase (101) surface
锐钛矿相TiO2(101)表面
1.
Electronic structures of nitrogen(N)/fluorine(F)-doped and N-F-codoped TiO2 anatase (101) surfaces were investigated by density functional theory (DFT) plane-wave pseudopotential method.
采用密度泛函理论(DFT)平面波赝势方法计算了N/F掺杂和N-F双掺杂锐钛矿相TiO2(101)表面的电子结构。
3) TiO_2 anatase phase
TiO_2锐钛矿相
4) Anatase TiO_2
锐钛矿TiO_2
1.
Effect of Gold Doping on the Photocatalytic Activity of the Anatase TiO_2;
Au掺杂方式对锐钛矿TiO_2光催化性能的影响
5) anatase
[英]['ænə,teis] [美]['ænə,tes]
锐钛矿相
1.
Study on Preparation, Modification and Photocatalytic Properties of Anatase Titania Nanoparticles with High Thermal Stability;
高热稳定性锐钛矿相纳米TiO_2的制备、改性及其光催化研究
2.
Pure anatase can be obtained without being sintered by controlling experimental conditions.
通过控制实验条件,可以得到单一的锐钛矿相TiO2纳米晶。
3.
Nanocrystalline anatase TiO2 powders were prepared by the method of precipitation-solution-gelation, using H2TiO3 as re-actants.
温度较低时,锐钛矿相的Raman谱峰明显可见,由于高温下Raman信号减弱,随着温度升高,Raman特征谱峰逐渐减弱以至于全部消失,仅显示出几个宽宽的凸起。
6) anatase phase
锐钛矿相
1.
The films remain completely the anatase phase and show better photocatalytics after being annealed to 550℃ in the air for an hour.
实验结果显示,用射频磁控溅射得到的纳米晶粒TiO2 薄膜与衬底结合紧密,薄膜表面致密、平整,经 550℃晶化的纳米晶粒TiO2 薄膜为均一的锐钛矿相,具有良好的紫外光吸收率。
2.
The nanometer Fe3+-TiO2 thin films transform into the anatase phase at 350-550℃.
退火温度在350-550℃时Fe3+-TiO2复合薄膜均为锐钛矿相,以石英玻璃为基片的掺铁TiO2复合膜在(101)面有一定的择优取向。
补充资料：锐钛矿
化学成分为TiO2、晶体属四方晶系的氧化物矿物。与金红石和板钛矿成同质三象（见同质多象）。除通常均呈尖锐的四方双锥晶形、具平行底面和锥面的中等解理、硬度和比重较低外，锐钛矿的其他物理性质、产出条件和用途都与金红石相似，但不如金红石稳定和常见。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。