1) incipient oxidation of metal surfaces
表面初始氧化
2) Initial oxidation
初始氧化
1.
The initial oxidation of uranium (U) in the atmosphere of O2 was studied by Auger elctron spectroscopy (AES) and electron energy loss spectroscopy (EELS) at different temperatures in a high vacuum chamber.
利用俄歇电子能谱(AES)和电子能量损失谱(EELS)研究了高真空室中不同温度下金属铀与氧的初始氧化过程,并分析了环境温度以及表面与界面的化学组成等因素对金属铀表面氧化过程的影响。
2.
The initial oxidation processes of niobium at normal temperature was studied with electron energy loss spectroscopy(EELS)and auger energy spectroscopy (AES) in this paper.
利用电子能量损失谱(EELS)和俄歇电子能谱(AES)研究室温下铌的初始氧化过程,研究表明:清洁表面铌的EELS的实验值与理论值较为符合;随着氧化程度的加剧,其体等离子体(BP)、表面等离子体(SP)以及价带间跃迁所造成的电子能量损失峰发生了明显的偏移和强弱的变化,也解释了Nb→NbO→NbO2的初始氧化过程;另外,铌在潮湿空气里氧化1周,在其表面只生成很薄一层的Nb2O5氧化层。
3) original surface film
初始表面膜
4) initialization list
初始化列表
1.
Studies the form of definitions to the constructor functions in the class of C++ composition class,analyzes the essential nature in using initialization list to initialize the data in composition class.
对C++组合类中构造函数的定义形式做了研究,分析了必须使用初始化列表来初始化组合类的数据成员的实质意义。
5) Initial dark oxidation
初始暗氧化
6) initialization list
初始化列表、初始值列表
补充资料：表面
表面
指人体或器官的外面或空腔的内面。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条