1) high manganese steel (TWIP/TRIP steel)
高锰钢(TWIP/TRIP钢)
3) TWIP/TRIP steel
TWIP/TRIP钢
1.
,on the basis of the research conclusions for weathering steel,ferritic stainless steel and TWIP/TRIP steel with high Mn in laborator.
对国内外钢的薄带铸轧技术发展情况进行了总结,结合实验室对耐侯钢、铁素体不锈钢和高锰TWIP/TRIP钢薄带铸轧的研究结论,对钢的薄带铸轧过程中的亚快速凝固和近终型成形引起的新的冶金学现象如表面负偏析、全等轴晶铸态组织以及消除带材边裂等进行了阐述,指出薄带铸轧有利于进一步提高材料性能。
4) SiMn TRIP steel
硅锰TRIP钢
1.
6×10-6s-1, total elongation of the high carbon SiMn TRIP steel increased from 14%～15% to about 22%; yield strength increased from 1 015MPa to 1 198MPa, and tensile strength from 1 448MPa to 1 546MPa, the volume fraction of retained austenite in tensile specimens was reduced.
68Mn高碳硅锰TRIP钢室温低应变速率下的拉伸性能。
5) Si-Mn TRIP Steel
硅锰系TRIP钢
6) TWIP steel
TWIP钢
1.
Deformed microstructure characteristics of Fe-28Mn-3Si-3Al TWIP steel;
Fe-28Mn-3Si-3Al TWIP钢变形的微观组织特征
2.
Effects of annealing temperature on microstructures and properties of the 25Mn-3Si-3Al-TWIP steel;
退火温度对25Mn-3Si-3Al-TWIP钢组织和力学性能的影响
3.
Properties and microstructure of TWIP steel used in automobiles;
汽车用TWIP钢的力学性能与微观组织
补充资料：高锰钢
分子式：
CAS号：
性质：工业中广泛应用的一种特殊耐磨钢，在大的冲击载荷下具有很高耐磨性，它的主要成分含碳1.0％～1.3％和锰11％～14％，锰碳含量比为10～12。这种钢机械加工困难，基本上都是以铸件形式使用。在使用中经受冷变形后，表层即产生显著硬化，最高硬度可达HB500～550，具有优良的耐磨性。广泛用于要求既耐磨又耐冲击的零部件。高锰钢除了具有良好的耐磨性以外，而且还具有良好的力学性能，不会冷脆；在受力变形时，能吸收大量能量，受到弹丸射击时也不易穿透，因此适宜于制造防弹板以及保险箱钢板等。
CAS号：
性质：工业中广泛应用的一种特殊耐磨钢，在大的冲击载荷下具有很高耐磨性，它的主要成分含碳1.0％～1.3％和锰11％～14％，锰碳含量比为10～12。这种钢机械加工困难，基本上都是以铸件形式使用。在使用中经受冷变形后，表层即产生显著硬化，最高硬度可达HB500～550，具有优良的耐磨性。广泛用于要求既耐磨又耐冲击的零部件。高锰钢除了具有良好的耐磨性以外，而且还具有良好的力学性能，不会冷脆；在受力变形时，能吸收大量能量，受到弹丸射击时也不易穿透，因此适宜于制造防弹板以及保险箱钢板等。