1) Melamine Formaldehyde
三聚氰胺甲醛
1.
First, Melamine Formaldehyde Moulding materials were prepared by Melamine Formaldehyde resin andα-cellulose.
本论文详细的研究了三聚氰胺甲醛模塑料的制备工艺,并以聚乙二醇和苯代三聚氰胺改性,制得性能良好的模塑料;最后通过改进工艺和使用甲醛捕捉剂,有效的降低了模塑料的甲醛释放量。
2) melamine-formaldehyde
三聚氰胺-甲醛
1.
Microcapsules were prepared by the method of in-siu polymerization with melamine-formaldehyde as the outer membrane and a phase change materials as core,which melt point was 24℃.
以三聚氰胺-甲醛为壁材,十二醇为囊芯,采用原位聚合法制备了相变储热微胶囊。
2.
The microencapsulated phase change materials were prepared with in situ polymerization using dodecanol as the core, melamine-formaldehyde resin as the shell.
本文采用原位聚合法以十二醇为芯材,以三聚氰胺-甲醛树脂为壁材,制备微胶囊相变材料并对其进行性能表征。
3) melamine-formaldehyde paper
三聚氰胺甲醛纸
4) melamine formaldehyde polycondensate (MF)
三聚氰胺甲醛缩聚物(MF)
5) 1,3,5-Triazine-2,4,6-triamine, polymer with formaldehyde, hydrochloride
甲醛聚三聚氰胺盐酸盐
6) melamine-formaldehyde resin
三聚氰胺甲醛树脂
1.
Study on melamine-formaldehyde resin modified with silicone;
有机硅改性三聚氰胺甲醛树脂的研究
2.
Modification of PVAc with melamine-formaldehyde resin;
三聚氰胺甲醛树脂改性聚醋酸乙烯酯共聚乳液的研究
3.
Study on the wet strength agent of cyclic urea prepolymer modified melamine-formaldehyde resin;
脲醛预聚体改性三聚氰胺甲醛树脂增湿强剂的研究
补充资料：三聚氰胺甲醛模塑粉
分子式：
CAS号：
性质：由三聚氰胺甲醛树脂，加入漂白α-纤维素和润滑剂，浸渍后进行干燥，加入颜料，经球磨、过筛制得三聚氰胺甲醛模塑粉。其主要性能：流动性（拉西格），140～220mm；挥发物质≤4%；弯曲强度60～80MPa；冲击强度（缺口）1.5～2kJ/m2；热变形温度140～155℃；吸水性（冷水）≤35～50mg；收缩率0.20～1%；可抽取甲醛，3～30mg/L；水中24h后绝缘电阻≥104～105MΩ；电气强度≥5.0～10MV/m；介质损耗≤0.08～0.2MHz。
CAS号：
性质：由三聚氰胺甲醛树脂，加入漂白α-纤维素和润滑剂，浸渍后进行干燥，加入颜料，经球磨、过筛制得三聚氰胺甲醛模塑粉。其主要性能：流动性（拉西格），140～220mm；挥发物质≤4%；弯曲强度60～80MPa；冲击强度（缺口）1.5～2kJ/m2；热变形温度140～155℃；吸水性（冷水）≤35～50mg；收缩率0.20～1%；可抽取甲醛，3～30mg/L；水中24h后绝缘电阻≥104～105MΩ；电气强度≥5.0～10MV/m；介质损耗≤0.08～0.2MHz。