2) TiO 2 colloid
二氧化钛(TiO2)胶体
3) colloidal TiO 2
二氧化钛胶体
1.
PSS/colloidal TiO 2 films and PDDA/colloidal SiO 2 films were deposited onto optic fibers and microscopy glass slides by using the electrostatic self assembly monolayer method, and the optical properties of the resulted films were investigated.
采用静电自组装技术在石英玻璃光纤和显微镜载玻片上制备了二氧化钛胶体与阴离子聚电解质 PSS、二氧化硅胶体与阳离子聚电解质 PDDA的复合薄膜 ,研究了薄膜的光反射性能 。
4) titania sol
二氧化钛溶胶
1.
The anatase TiO 2 nanosized microcrystals were successfully prepared by the solvothermal crystallization of titania sol.
采用二氧化钛溶胶溶剂热晶化法成功制备了锐钛矿型TiO2 纳米微晶 ,研究了不同制备条件对TiO2 晶型和粒径的影响 ,并用XRD、TEM、TG -DTG -DTA进行表征 结果表明 ,制得的TiO2 纳米微晶粒径小、粒度均匀、热稳定性好、纯度高、单分
6) titania gel
二氧化钛凝胶
1.
The attachment, proliferation and differentiation of MC3T3-E1 osteoblast-like cells were studied on polished Ti (PT), roughened Ti (SAT) and the amorphous titania gel layer, which was formed by treatment Ti substrates with H_2O_2/HCL solution, coated roughened Ti substrates (SAHT).
以往研究表明用H_2O_2／HCl溶液和400℃加热一小时处理钛金属表面能形成带有大量活跃羟基功能团(—OH)锐钛矿晶型的二氧化钛凝胶层，它能够在模拟体液中诱导羟磷灰石颗粒生成，提示其可能具有一定的生物活性。
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。