1) localized corrosion morphology
局部腐蚀形态
2) local corrosion
局部腐蚀
1.
The testing and evaluation of the local corrosion caused by CO2 has been remaining a bottleneck in the field of corrosion science and engineering.
局部腐蚀测试及评价一直是困扰腐蚀界的一大难题。
2.
While for the local corrosion of the bolts, it was the joint result of the high spe.
对某炼化厂再生塔底重沸器的失效原因进行了分析 ,根据外观检测、材料成分分析、金相分析和腐蚀产物成分分析一系列检测结果判定 ,不锈钢换热管是由于H2 S和CO2 加上介质冲刷破坏了钝化膜引起的孔蚀 ,浮头螺栓的局部腐蚀则是由于蒸汽高速冲刷和H2 S共同作用的结果 ,最后根据失效原因提出了防止和改进措
3) localized corrosion
局部腐蚀
1.
A study on the mechanism of localized corrosion of stainless steel by tungstate;
钨酸根对不锈钢局部腐蚀的作用
2.
Coupled multielectrode array sensors for localized corrosion monitoring;
耦合多电极矩阵传感器在局部腐蚀监/检测中的应用
3.
In this work,the scanning microelectrode technique and potentiodynamic polarization were used to study the localized corrosion behavior of the reinforcing steel in simulated concrete pore solution with different pH values and chloride ion concentrations.
应用扫描微电极法原位测量了模拟混凝土孔隙液中钢筋表面微区的电位分布,并结合动电位极化曲线的测量,研究了钢筋的局部腐蚀行为及模拟混凝土孔隙液pH值和Cl-浓度对它的影响。
4) partial corrosion
局部腐蚀
1.
The results indicate that the corrosion resistance of coatings with good quality are advanced, and flaws in coatings will result in partial corrosion in A3 steel.
认为当镀层质量较好时,耐蚀性较强,但如果镀层存在缺陷,则易引起底材局部腐蚀;双层镀对抑制局部腐蚀有利。
5) Corrosion morphology
腐蚀形态
1.
The influence of cerium on depletion layer of the surface of Al Li alloys and the influence of the depletion layer on the corrosion morphology of the alloys were studied.
研究了稀土元素铈对铝锂合金表面贫化层的影响以及表面贫化层对合金腐蚀形态的影响。
6) morphological erosion
形态腐蚀