2) maleation
马来酸酐化
3) maleic anhydride single-ester
半酯化马来酸酐
4) phosphonated polymaleic anydride
膦化聚马来酸酐
5) maleic acid
马来酸酐
1.
Synthesis mono polyethylene glycol maleate with maleic acid and polyethylene glycol analysis the influencing factors of the reaction,through test,it was found:under condition of existence of self-made catalyst,Fix mol ratio of polyethylene to glycol maleic acid at 2.
由马来酸酐与聚乙二醇单甲醚合成马来酸双聚乙二醇单甲醚酯,对其影响因素进行分析,通过试验确定在自制复合催化剂条件下,当聚乙二醇单甲醚∶马来酸酐摩尔比为2。
2.
The effect of the grafting of maleic acid (MAH) onto chlorinated polypropylene(CPP) on the surface property was studied.
研究了马来酸酐在氯化聚丙烯分子链上的接枝对其表面性质的影响,探讨了马来酸酐接枝氯化聚丙烯与聚丙烯及金属的粘接作用及耐水性。
3.
The technology for synthesizing of polyaspartic acid with maleic acid as raw material was studied in the three steps of ammonification, polymerization and hydrolyzation.
对以马来酸酐为原料合成聚天冬氨酸的工艺路线分为胺化、聚合、水解三个步骤进行了研究,分别考察三步反应的温度、时间和原料配比条件对产物的平均分子量和阻垢性能的影响,研究结果表明胺化反应最适宜的反应条件是原料配比为MA∶NH3=1∶3,反应时间6h,温度为80℃;聚合反应最适宜的反应温度是230℃,时间是3h;水解反应适宜的温度和时间分别是50℃和30min。
6) MAH
马来酸酐
1.
Study on down-powder grafted with MAH;
马来酸酐接枝羽绒粉体的研究
2.
Study of Graft Modification of PP by MAH;
马来酸酐接枝聚丙烯的研究
3.
STUDIES AND APPLICATIONS OF THE SOLID- PHASE GRAFTING OF MAH AND St ONTO PP;
马来酸酐、苯乙烯双单体固相接枝聚丙烯及其应用
补充资料：马来酸
HOOCCH=CHCOOH
分子量 116．0 7
无色可燃结晶体。有令人不愉快的酸气味、味涩。密度1．590g／cm3。熔点130．5℃。易溶于水和乙醇，能溶于丙酮、冰醋酸，微溶于醚和苯。135℃以上分解，温度高于熔点时部分转变为反丁烯二酸。有腐蚀性，低毒。
应用 主要用于有机合成，用于制取不饱和聚酯树脂、酒石酸、反丁烯二酸、琥珀酸、农药、染色助剂和油脂防腐剂。也用于碱量法分析。
分子量 116．0 7
无色可燃结晶体。有令人不愉快的酸气味、味涩。密度1．590g／cm3。熔点130．5℃。易溶于水和乙醇，能溶于丙酮、冰醋酸，微溶于醚和苯。135℃以上分解，温度高于熔点时部分转变为反丁烯二酸。有腐蚀性，低毒。
应用 主要用于有机合成，用于制取不饱和聚酯树脂、酒石酸、反丁烯二酸、琥珀酸、农药、染色助剂和油脂防腐剂。也用于碱量法分析。