1) PS microspheres
PS微球
1.
The effects of reaction temperature,stirring rate and amount of the pH stabilizer on size and monodispersity of the PS particles were investigated by orthogonal experiment method,and the reaction conditions used to prepare 600~1000 nm monodisperse PS microspheres were optimized.
以NaHCO3/Na2CO3为pH稳定剂和离子强度调节剂,用无皂乳液聚合法合成了亚微米级聚苯乙烯(PS)微球,用正交实验考察不同因素对合成聚合物微球粒径及粒径分布的影响,优化制备600~1000nm单分散PS微球的工艺条件,放大批量制备了标称粒经是600,800和1000nm的PS微球,合成的PS微球球形度好,相对标准偏差小,均匀性和稳定性都满足国家一级粒度标准物质的要求。
2) cross linked polystyrene microsphere
交联PS微球
1.
Monodisperse cross linked polystyrene microspheres of 60～200 nm diameters were prepared by emulsion polymerization.
采用乳液聚合法合成一系列粒径在 60～ 2 0 0 μm间的单分散交联PS微球 ,并探讨影响乳液聚合稳定性、粒径大小及微球单分散性的因素。
3) PS nanosphere
PS纳米微球
4) modified PS microsphere
改性PS大孔微球
5) PS-PMMA microemulsion spheres
PS-PMMA纳米微乳液球
6) PS/SiO_2 nanocomposite microspheres
PS/SiO2纳米复合微球
1.
The influences of the content of the PVP,NH_4OH,and tetraethyl orthosilicate(TEOS) on the size and morphology of the PS/SiO_2 nanocomposite microspheres were investigated.
研究了PVP,NH4OH和原硅酸乙酯(TEOS)的用量对PS/SiO2纳米复合微球尺寸和形态的影响。
补充资料：PS
分子式：
CAS号：
性质：为苯乙烯均聚物。无色透明、高光泽。加工性、着色性、刚性和电绝缘性良好，但质脆易裂。耐酸碱、氧化还原剂、醇类和洗涤剂，不耐烃类和氯烃类溶剂。拉伸强度36～52MPa，弯曲模量2620～3380MPa，悬臂梁缺口冲击韧性19～24J/m。热变形温度76～94℃。体积电阻率1017～1019Ω·cm，介电常数(50～106Hz)2.2～2.7，介质损耗正切(50～106Hz)0.0001～0.0002，介电强度19.7kV/mm。系由苯乙烯在引发剂存在下进行自由基聚合得到。工业生产均用连续本体聚合法。主要用作音像制品和光盘磁盘盒，灯具和室内装饰件，高频电绝缘零件。其双轴取向薄膜为包装和电器工业的主要材料。
CAS号：
性质：为苯乙烯均聚物。无色透明、高光泽。加工性、着色性、刚性和电绝缘性良好，但质脆易裂。耐酸碱、氧化还原剂、醇类和洗涤剂，不耐烃类和氯烃类溶剂。拉伸强度36～52MPa，弯曲模量2620～3380MPa，悬臂梁缺口冲击韧性19～24J/m。热变形温度76～94℃。体积电阻率1017～1019Ω·cm，介电常数(50～106Hz)2.2～2.7，介质损耗正切(50～106Hz)0.0001～0.0002，介电强度19.7kV/mm。系由苯乙烯在引发剂存在下进行自由基聚合得到。工业生产均用连续本体聚合法。主要用作音像制品和光盘磁盘盒，灯具和室内装饰件，高频电绝缘零件。其双轴取向薄膜为包装和电器工业的主要材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条