1) stainless steel powders and silkscreen
不锈钢粉末与丝网
1.
Pore and permeation of composite of stainless steel powders and silkscreen were researched, which depended on the particle size, especially that of the last layer.
不锈钢粉末与丝网复合的孔隙和透过性能研究表明,料浆粒度显著影响孔隙和透过性能,末级料浆粒度起决定性作用;二次双向涂覆时,相同料浆粒度料浆形成外细内粗的三明治结构,不同粒度料浆形成由粗到细的梯度结构;复合多孔材料具有均匀的孔径分布和高透过率。
2) stainless steel powder
不锈钢粉末
1.
Effects of vacuum sintering and dissociated ammonia sintering on the properties of 316 L and 304 L stainless steel powders were studied.
研究了真空和分解氨气氛对316L和304L不锈钢粉末烧结性能的影响。
3) powder-formed stainless steel
粉末不锈钢
4) stainless steel wire mesh
不锈钢丝网
1.
The effect of preparation parameters on the structure and catalytic performance of Ce-Pt-Pd/SSWM stainless steel wire mesh catalyst
制备参数对不锈钢丝网催化剂结构和性能的影响
5) stainless wire mesh
不锈钢网丝
1.
Analysis present that pitting corrosion and stress corrosion are the mainly reasons for the crack of stainless wire mesh.
结果表明,不锈钢网丝的点腐蚀和应力腐蚀是造成网丝断裂的根本原因,由于不锈钢网丝的断裂,导致波纹管失去丝网的保护和轴向伸长的约束,波纹管在内压作用下冲破丝网的约束,进而产生过度弯曲变形,在波纹管与短接管焊接的薄弱处因过载而发生断裂。
6) 316L stainless steel powder
316L不锈钢粉末
1.
Electron beam selective melting of 316L stainless steel powder;
316L不锈钢粉末的电子束选区熔化成形
2.
The forming mechanism for the crack produced in the process of laser forming 316L stainless steel powder alloy has been studied in the paper by micro measurements.
采用微观测试分析方法,针对316L不锈钢粉末,深入研究了激光快速成形过程中熔覆层的开裂行为及其形成机理。
补充资料：不锈钢粉
分子式：
CAS号：
性质：由不锈钢合金制得的金属颜料。粒子形状为不规则的片状，密度7.55g/cm3，平均粒径<33μm。有良好的耐腐蚀性和耐久力，其片状粒子可以平行涂膜表面定位并且分布在整个涂膜中，形成具有优良遮盖力的屏蔽层，把湿气挡住。不锈钢粉采用低碳钢即含铬18％～20％，镍10％～12％，钼约3％的不锈钢为原料，经雾化后，在润滑剂(硬脂酸)存在下球磨、过筛分级制成颜料，也可直接进行湿球磨。主要用于维护保养涂料、耐热和耐久性涂料，不锈钢片状颜料在装饰性漆中可产生极有吸引力的天然金属色。
CAS号：
性质：由不锈钢合金制得的金属颜料。粒子形状为不规则的片状，密度7.55g/cm3，平均粒径<33μm。有良好的耐腐蚀性和耐久力，其片状粒子可以平行涂膜表面定位并且分布在整个涂膜中，形成具有优良遮盖力的屏蔽层，把湿气挡住。不锈钢粉采用低碳钢即含铬18％～20％，镍10％～12％，钼约3％的不锈钢为原料，经雾化后，在润滑剂(硬脂酸)存在下球磨、过筛分级制成颜料，也可直接进行湿球磨。主要用于维护保养涂料、耐热和耐久性涂料，不锈钢片状颜料在装饰性漆中可产生极有吸引力的天然金属色。