This paper researches the factors influencing CNTS dispersion by using experimental method,and based on the research results,points out that the CNTS dispersion could be improved by ultrasonic oscillations and adding right amount of sodium dodecyl sulfate or sodium dodecyl benzene sulfate can disperse it better.

Through orthogonal experimental design,the preparation of iron oxide nanometer particles by ultrasonic-solid phase reaction was studied.

The optimum conditions were as follows:PVA 3g,H_2O 20mL,H_2SO_4 8g,ultrasonic vibration 80min,reaction temperature 55℃.

The use of ultrasonic vibration in acetic acid extraction of Ca2+ from wollastonite increased obviously the extraction ratio of Ca2+ ion.

0 nm has been prepared with the sol-gel method,and use ultrasonic surge.

By using ammonium phosphotungstste (NH4)3[PW12O40], diammonium hydrogen phosphate (NH4)2HPO4 and self-MCM-41 as the raw material, tungsten phosphide (WP) and MCM-41-supported WP catalysts (WP/MCM-41) were prepared by temperature-programmed reduction with H2 under ultrasonic oscillation.

The heat cured sand of Al-Mg-B compound phosphate inorganic binder was modified by ultrasonic oscillation to binder and adding organic polymer YPPJ while mixing of sand.