1) Pencil-Tip Shaped Fracture
笔尖状断裂
1.
Analysis on Pencil-Tip Shaped Fracture of Cord Steel 72A during Cold Drawing and Improvement of Process
72A帘线钢线材冷拔笔尖状断裂分析和改进工艺措施
2) sharp fracture
尖状断口
1.
The main cause of martensite formation in central part of wire rod is central segregation in the bloom as determined by this study and martensite makes sharp fracture of the wire rod.
研究了不同铸坯中心偏析成分在控冷过程中的相变行为,结果表明,铸坯中心成分偏析是导致高碳钢盘条中心出现马氏体的主要原因,而马氏体又是导致盘条拉伸出现尖状断口的主要原因;铸坯中心碳偏析指数不能超过1。
3) fracture process zone at crack tip
裂尖断裂过程区
1.
The experimental results of pyromagnetic effect revealed in the rupture process of rheological material with defects make known that:owing to the existence of internal temperature gradient leads to the occurrence of pyromagnetic effect in the fracture process zone at crack tip.
带缺陷流变性材料破坏过程中显现出热致磁效应的实验结果表明：在材料破坏的过程中，由于内部温度梯度的存在，导致裂尖断裂过程区具有热致磁效应。
4) Fracture Behavior at Crack Tip
裂尖断裂行为
5) feather fracture
羽状断裂
6) ring fractures
环状断裂
1.
It is characterized by peculiar geomorphology associated with perfect ring fractures and radial dykes.
火山机构呈特殊的环状地貌特征， 周围发育明显的环状断裂和放射状岩墙， 并由爆发相、喷溢相、火山颈相和侵入相４ 种岩相构成， 表现出一种爆发－ 喷溢－ 侵入的简单的火山活