3) Slag-washing Water of BF
高炉冲渣水
4) water rushing waste material system
水冲渣系统
1.
Aiming at the closed loop control problem of water rushing waste material system for making iron-out in furnace,this paper pointed out it was difficult to realize auto tracing iron making waste material by means of adjusting water quantity.
针对一类高炉出铁水冲渣系统难以实现冲水量自动跟踪炼铁废料量的闭环控制问题,提出了采用基于仿人智能的自适应控制策略,讨论了控制结构模式、任务与参数自适应控制算法。
5) Blast furnace system
高炉系统
6) blast furnace slag
高炉炉渣
1.
Alumina content in Nanjing Steel blast furnace slag is up to 19%,which results in worse slag fluidity,higher furnace operating temperature and higher silicon content of hot metal.
南京钢铁集团公司高炉炉渣中氧化铝含量高达19%,因此炉渣流动性变差,高炉被迫采用高温操作,铁水硅含量偏高,影响了高炉的强化。
2.
The measurementand systemat-ic study had been made on chemical components,mineral compositions,mineral structure,viscosity and melting tem-perature of the blast furnace slag.
试验选取生产现场的高炉炉渣作为基准原料,对现场高炉炉渣和高炉初渣的化学成分、矿物组成、矿物结构以及粘度和熔化性温度进行了测定和系统研究。
3.
INBA is a new type of blast furnace slag processing technology,can be converted to high - grade blast furnace slag cement materials,the recycling of slag implementation.
INBA法是一种新型高炉炉渣处理技术,可以将高炉废渣转为高品位的水泥原材料,实现炉渣的再生利用。
补充资料：高炉泡沫渣
高炉泡沫渣
the foaming slag of blast furnace
一定值后会有大量气体以气泡形式分散于渣中使炉渣的体积膨胀‘这种炉渣即为泡沫渣，它是特殊矿冶炼高炉造渣的一个重要问题。泡沫渣的产生将造成高炉生产过程渣铁出不尽，料柱透气性恶化，风口易挂渣，给高炉炉况顺行和强化带来困难。当炉渣进入渣罐后由于其体积膨大使渣罐利用率降低，甚至从渣罐上部溢出，造成事故。泡沫渣的形成有两个条件，一是有大量的分散气体生成，二是炉渣性能使分散气体稳定存在，从而使渣中气体量不断增加。在钒铁磁铁矿的高炉冶炼中，高炉下部有较多的Feo、TIO:等氧化物从渣中还原，从而产生大量CO气体。同时，高钦型高炉渣表面吸附，富集的活性物质比普通渣高得多。表面活性物.的存在使液膜的表面私度比体积豁度高，从而阻碍了排气速度，延长了泡沫的寿命。表面活性物的存在又使炉渣表面张力大大下降，造成渣内分散气泡合并上浮困难，使气泡更稳定，从而形成泡沫渣。解决泡沫渣间题的办法是采用一切手段提高渣中“氧势”，抑制TIOZ还原，减少Ti(C、N)等胶质微粒的生成，也即减少表面吸附的活性物质量，从而阻止泡沫形成。goolu Paomozha高炉泡沫渣(the foaming、lag。f blast fur-nace)高炉冶炼钒钦磁铁矿时，炉渣中Tio。高达
说明：补充资料仅用于学习参考，请勿用于其它任何用途。