1) Al-Ti-Ce ternary layers
![点击朗读](/dictall/images/read.gif)
Al-Ti-Ce三元渗层
1.
Al-Ti binary layers and Al-Ti-Ce ternary layers were prepared on the surface of martensitic valve steel 4Cr10Si2Mo by solid powder method.
用固体粉末法在4Cr10Si2Mo马氏体气阀钢表面制备了Al-Ti二元渗层及Al-Ti-Ce三元渗层,研究了渗层的显微组织和成分分布,测定了渗层显微硬度。
2) Al-Cr-Ce ternary layers
![点击朗读](/dictall/images/read.gif)
Al-Cr-Ce三元渗层
1.
Al-Cr binary layers and Al-Cr-Ce ternary layers coatings have been deposited on the surface of martensitic valve steel 4Cr10Si2Mo by solid powder method.
用固体粉末法,在4Cr10Si2Mo马氏体气阀钢表面制备了Al-Cr二元渗层及Al-Cr-Ce三元渗层,研究了渗层的显微组织和成分分布,测定了渗层由表及里的显微硬度。
4) Al-Ti binary layers
![点击朗读](/dictall/images/read.gif)
Al-Ti二元渗层
1.
Al-Ti binary layers and Al-Ti-Ce ternary layers were prepared on the surface of martensitic valve steel 4Cr10Si2Mo by solid powder method.
用固体粉末法在4Cr10Si2Mo马氏体气阀钢表面制备了Al-Ti二元渗层及Al-Ti-Ce三元渗层,研究了渗层的显微组织和成分分布,测定了渗层显微硬度。
5) Ce-Co-Al ternary system
![点击朗读](/dictall/images/read.gif)
Ce-Co-Al三元系
6) Ce-Al-Cu system
![点击朗读](/dictall/images/read.gif)
Ce-Al-Cu三元系
1.
Based on the constructed phasecomposition regions of the Ce-Al-Cu ternary system,it reveals that the compositionregion of the bulk glass alloys in the Ce-Al-Cu system falls in the Ce-rich phase regionswithα-Ce_3Al as the common phase.
与Ce-Al-Cu三元系平衡相图相比较而言,对传统电弧熔炼得到的熔铸态样品的相成份确定,可以为非晶金属塑料(AMP)的形成机制提供更好的数据信息。
补充资料:Al
元素符号: al 英文名: aluminum 中文名: 铝
相对原子质量: 26.9815 常见化合价: +3 电负性: 1.61
外围电子排布: 3s2 3p1 核外电子排布: 2,8,3
同位素及放射线: al-26[730000y] *al-27 al-28[2.3m]
电子亲合和能: 48 kj·mol-1
第一电离能: 577.6 kj·mol-1 第二电离能: 1817 kj·mol-1 第三电离能: 2745 kj·mol-1
单质密度: 2.702 g/cm3 单质熔点: 660.37 ℃ 单质沸点: 2467 ℃
原子半径: 1.82 埃 离子半径: 0.51(+3) 埃 共价半径: 1.18 埃
常见化合物: al2o3 alcl3 al2s3 naalo2 al2(so4)3 al(oh)3
发现人: 厄斯泰德、维勒 时间: 1825 地点: 丹麦
名称由来:
拉丁文:alumen, aluminis(铝)。
元素描述:
柔软轻质的银白色金属,在地壳中含量第三。
元素来源:
自然界完全没有铝单质存在。可以电解铝土(al2o3)制取铝。
元素用途:
上自飞机下到易拉罐应用广泛。因为纯铝太柔软,所以要加入不到1%的硅或铁以加大其硬度和强度。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条