1) superparamagnetic CoFe2O4 nanoparticles
超顺磁CoFe2O4纳米颗粒
1.
The superparamagnetic CoFe2O4 nanoparticles with core size of 5-10nm were prepared by high temperature polyol process using FeCl3·6H2O,CoCl2·6H2O and HOOC-PEG-COOH as reactants.
6H2O和HOOC-PEG-COOH为反应物,利用高温多元醇法制备了核心粒径为5～10nm的超顺磁CoFe2O4纳米颗粒,样品在水溶液中具有良好分散性。
3) superparamagnetic Fe_3O_4 nanoparticles
超顺磁性Fe3O4纳米颗粒
1.
The superparamagnetic Fe_3O_4 nanoparticles with core size of 5～10 nm were prepared by polyol process at high temperature.
利用高温多元醇方法制备了核心粒径为5～10nm的超顺磁性Fe3O4纳米颗粒,并且样品在水溶液中具有良好分散性。
4) Fe_3O_4MNP
超顺磁性四氧化三铁纳米颗粒
1.
Fe_3O_4MNP was evaluated as a kind of plasmid pYDS-P53 carrier and transfected into U251 cell and BTSC.
目的:制作超顺磁性四氧化三铁纳米颗粒,从脑胶质瘤细胞中诱导培养出BTSC,以上述制备的纳米颗粒为载体将wt-p53基因转染入U251及BTSC中,来研究野生型p53基因对U251细胞及BTSC生长及放疗敏感性的影响。
5) CoFe 2O 4 ultrafine particle
CoFe2O4纳米微粒
6) CoFe2O4 nano-particles
CoFe2O4纳米粒子
1.
Magnetic measurements show that the coercivity of CoFe2O4 nano-particles increases with the increasing of grain size,the coercivity of CoFe2O4 nano-particles of 9.
采用共沉淀方法制备了一系列CoFe2O4纳米粒子。
补充资料：超顺磁性
铁磁性物质的颗粒小于临界尺寸时，外场产生的磁取向力不足以抵抗热骚动的干扰，其磁化性质与顺磁体（见顺磁性）相似，称作超顺磁性。临界尺寸与温度有关，例如球状铁粒在室温的临界半径为12.5纳米，而在4.2K时半径为2.2纳米还是铁磁性的。
超顺磁体的磁化曲线与铁磁体不同，没有磁滞现象。当去掉外磁场后，剩磁很快消失。如以H/T（H是磁场强度,T是绝对温度）为坐标横轴，不同温度的磁化曲线合而为一，可用顺磁体的磁化公式（朗之万函数或布里渊函数）表示。外加磁场时，在普通顺磁体中，单个原子或分子的磁矩独立地沿磁场取向；而超顺磁体以包含大于105个原子的均匀磁化的单畴作为整体协同取向,所以磁化率较一般顺磁体大很多。
超顺磁体的磁化曲线与铁磁体不同，没有磁滞现象。当去掉外磁场后，剩磁很快消失。如以H/T（H是磁场强度,T是绝对温度）为坐标横轴，不同温度的磁化曲线合而为一，可用顺磁体的磁化公式（朗之万函数或布里渊函数）表示。外加磁场时，在普通顺磁体中，单个原子或分子的磁矩独立地沿磁场取向；而超顺磁体以包含大于105个原子的均匀磁化的单畴作为整体协同取向,所以磁化率较一般顺磁体大很多。