1) Indentation
[英][,ɪnden'teɪʃn] [美]['ɪndɛn'teʃən]
压痕开裂
1.
Singular Stress Fields and Fracture for Periodic-Arrayed Indentation(Part Ⅱ:Critical Load for Cracking)
周期阵列压痕奇异应力场与开裂(Part Ⅱ:压痕开裂临界载荷)
2) indentation crack
压痕裂纹
1.
The propagation process of indentation crack in air of different relative humidity(2%,30%,98%) for a poled PZT-5 ferroelectric ceramic was investigated.
在不同湿度(2%、30%、98%)的空气中,研究了极化的锆钛酸铅(PZT-5)铁电陶瓷压痕裂纹在残余应力、电场作用下的滞后扩展。
2.
Domain switching and propagation of an unloaded indentation crack for BaTiO_3 single crystal under residual stress and applied stress in humid air and water have been in situ investigated.
原位研究了残余应力和外加应力导致 BaTiO_3单晶压痕裂纹在湿空气和水中的滞后扩展及畴变。
3.
The experiment of a coupling effect on propagation of unloaded indentation cracks in a PZT-5H ceramic shows that residual stress itself is too small to induce delayed propagation of the indentation crack in silicon oil.
通过在硅油中加恒电场实验,研究了PZT-5H铁电陶瓷Vickers压痕裂纹的扩展行为,探讨了电场、残余应力以及介质间的耦合作用。
3) indentation-fracture method
压痕-断裂法
4) Indentation fracture technique
压痕断裂法
5) vickers indentationcrack
维氏压痕裂纹
6) indentation fracture mechanics
压痕断裂力学
补充资料：压痕
压痕
rolled pit
yahen压痕(r olled pit)钢材表面缺陷之一，系产品表面上被外物压成的局部凹坑，呈周期性单个或多个断续分布。一般产品表面允许有深度不超过标准规定的压痕。 产生原因是:(1)周期性压痕是由于成品孔或成品前孔、矫直辊、出口辊动导板(见导板)、导辊等粘有凸起物;(2)异物掉在轧件上，经轧后脱落;(3)产品在运送、保管过程中与硬物碰压或产品本身相互格压。 防止和消除办法有:(l)生产中定期检查轧件、轧糟、矫直辊和辊动导板，发现问题及时处理;(2)轧制时防止异物掉在轧件上;(3)吊运产品要平稳，产品包装要平齐，捆扎要牢固，堆放底脚要垫平。 (刘肾才)