1) CB/silica incorporation
炭黑/白炭黑并用
1.
The best CB/silica(the incorporation ratio was 75/25 and 50/50) incorporation sequence was discussed in the paper through changing CB/silica incorporation sequence.
结果表明,炭黑、白炭黑的加入顺序并不是绝对的,炭黑/白炭黑并用比为75/25时(填料总量为45份),先加白炭黑有利于白炭黑的分散,硫化胶物理机械性能较好,压缩生热较低,动态力学性能较好;当炭黑/白炭黑并用比为50/50时,炭黑/白炭黑一起加入得到的硫化橡胶性能较好。
2) silica
[英]['sɪlɪkə] [美]['sɪlɪkə]
白炭黑
1.
Comparison of polyolyfine elastomer vulcanizates reinforced by carbon black and silica;
炭黑与白炭黑增强聚烯烃弹性体硫化胶的比较
2.
Ecological utilization of oil shale by preparing silica and alumina;
生态化利用油页岩制备白炭黑和氧化铝
3.
Filler network and dynamic viscoelastic properties of silica/solution polymerized styrene-butadiene rubber composites;
白炭黑/溶聚丁苯橡胶复合材料的填料网络结构与动态黏弹性能
3) silica white
白炭黑
1.
Research of producing silica white through light silicon ash lime sintering and acid dissolving;
微硅粉生石灰煅烧酸溶制作白炭黑的研究
2.
Modified room temperature vulcanized silicone rubber adhesive filled in situ with silica white;
白炭黑原位填充的改性室温硫化硅橡胶胶黏剂
3.
Study on preparation of silica white from scrap rice hull;
废稻壳制白炭黑工艺研究
4) white carbon
白炭黑
1.
The research progress of preparation of white carbon by traditional chemical precipitation method;
传统沉淀法制白炭黑的研究进展
2.
Study of the influence about surface active agent to carbonation white carbon;
表面活性剂对碳化法制备白炭黑的影响研究
3.
Study on extractionof white carbon from kaolinby microwave catalysis;
微波催化从滇南高岭土中提取活性白炭黑
5) silica aerogel
白炭黑
1.
Effect of content of silica aerogel and boron-phenolic resin on properties of EPDM/NBR flexible insulation material;
白炭黑与硼酚醛树脂用量对EPDM/NBR柔性绝热层材料性能的影响
2.
Study on the control of process parameters in preparing nano-silica aerogel with precipitation method;
沉淀法制备纳米白炭黑工艺参数的控制
3.
Additive in deposition method of making nano-silica aerogel;
纳米白炭黑制备用添加剂
6) white carbon black
白炭黑
1.
Study on preparation and application of Ag-antibacterial white carbon black;
载Ag白炭黑抗菌剂的制备及应用研究
2.
Preparation of white carbon black using aluminum sulfate fag-end;
以硫酸铝废渣为原料制备白炭黑的工艺研究
3.
Study on cu-antibacterial white carbon black after improving performance;
铜型抗菌白炭黑的改性研究
补充资料：白炭黑
SiO2·nH2O
性状 白色高度分散的无定形粉末或絮状粉末。熔点1750℃。不溶于水和酸。空气中吸收水分后成为聚集的细粒。溶于氢氧化钠和氢氟酸。对其他化学药品稳定，耐高温，不燃烧。具有很高的电绝缘性。多孔性，内表面积大，在生胶中有较大分散力。
应用领域 主要用于橡胶工业，作为制造浅色橡胶制品最良好的补强剂和填充剂，虽然它的补强性能次于硬质碳黑，但由于颜色是白的，能解决使用碳黑会影响橡胶制品的美观和不能着色的缺点。涂料工业可用于油漆中以防止颜料沉淀。油脂工业用于制造润滑油脂。最细的粉末还用于纺织工业作为纤维的补强剂使用。另外，在油墨制造等方面也有一定的用途。
性状 白色高度分散的无定形粉末或絮状粉末。熔点1750℃。不溶于水和酸。空气中吸收水分后成为聚集的细粒。溶于氢氧化钠和氢氟酸。对其他化学药品稳定，耐高温，不燃烧。具有很高的电绝缘性。多孔性，内表面积大，在生胶中有较大分散力。
应用领域 主要用于橡胶工业，作为制造浅色橡胶制品最良好的补强剂和填充剂，虽然它的补强性能次于硬质碳黑，但由于颜色是白的，能解决使用碳黑会影响橡胶制品的美观和不能着色的缺点。涂料工业可用于油漆中以防止颜料沉淀。油脂工业用于制造润滑油脂。最细的粉末还用于纺织工业作为纤维的补强剂使用。另外，在油墨制造等方面也有一定的用途。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条