1) Li and Mg
锂、镁
2) Mg-Li alloy
镁锂合金
1.
Preparation of Conversion Coating with Cr free on Mg-Li Alloy;
镁锂合金无铬转化膜的制备工艺研究
2.
A chromium-free chemical conversion coating for Mg-Li alloy by phytic acid solution;
镁锂合金无铬植酸化学转化膜研究
3.
EIS analysis of Mg-Li alloy corrosion in alkaline condition;
镁锂合金碱性条件下腐蚀的EIS分析
3) Mg-Li alloys
镁锂合金
1.
The Study of Smelting Technology and Microstructures and Mechanical Properties of Mg-Li Alloys;
镁锂合金熔铸工艺及组织性能的研究
2.
Micro-arc oxidation (MAO) coatings have been successfully prepared on Mg-Li alloys by micro-arc oxidation.
利用微弧氧化技术在镁锂合金的表面成功制备了微弧氧化膜。
4) ratio of magnesium to lithium
镁锂比
5) magnabrite
锂镁皂土
1.
Its commercial products Veegum and magnabrite have been sold all over the world and they occupy a unique international market and their economic return are great now, this kind of montmorilloint has also been found in Yushugou, Tuokexun county of Xinjiang, China.
介绍了稀缺且具有极大经济价值的特殊粘土类矿产资源———锂镁皂土 (汉克托石 ,hec torite)的基本概念、形成机理、特性及开发利用概况。
6) magnesium-lithium alloy
镁锂合金
1.
The TC coefficients of the novel magnesium-lithium alloys were measured and the results showed the relationship between the thermal conductivity with alloying and heat treated states of alloys.
利用该设备对新开发的镁锂合金的导热系数进行了测量,反映了合金含量与导热性能之间的规律,能够满足对新型合金热物理性质及其影响因素的探索研究。
2.
In order to find a technique that can obviously improve the strength of magnesium-lithium alloy,an alpha-beta biphase coexistent magnesium-lithium alloy was designed according to the Mg-Li phase diagram and the effect of Al.
为了找到一种可以显著提高镁锂合金强度的工艺,根据镁-锂二元合金相图及铝元素在合金中的作用,设计了一种α(Mg)、β(Li)两相共存的镁锂合金(Mg-6Li-3Al),并进行了挤压和轧制;用光学显微镜和X射线衍射仪对合金不同状态的组织及性能进行了研究。
3.
Electroless nickel plating on magnesium-lithium alloy was studied,and an appropriate pretreatment was determined.
对镁锂合金化学镀镍进行了研究,确定了合适的前处理工艺。
补充资料：镁锂合金
分子式：
CAS号：
性质：以镁为基加入金属锂组成的合金。一般含锂15%以上。密度1.14～1.57g/cm3。为当今最轻的结构材料。比强度高于常规镁合金。强度220～340MPa。弹性模量40GPa。阻尼容量高，减震能力强。具有良好的冷、热加工性能。用熔铸法制取。用于航天航空器零件及其他高速动转器的零件制造。
CAS号：
性质：以镁为基加入金属锂组成的合金。一般含锂15%以上。密度1.14～1.57g/cm3。为当今最轻的结构材料。比强度高于常规镁合金。强度220～340MPa。弹性模量40GPa。阻尼容量高，减震能力强。具有良好的冷、热加工性能。用熔铸法制取。用于航天航空器零件及其他高速动转器的零件制造。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。