1.
The alloys occur ductile fracture after annealing.
合金热轧态呈脆性准解理断裂,退火后转变为韧性断裂。
2.
The fracture mode changed from quasi-cleavage plus cleavage obtaioed from conventional treatment to quasi-cleavage plus dimple.
微观断口由常规工艺的准解理加解理断裂变为准解理加韧?断裂。
3.
The tesile fracture is mixture of quasicleavage and touph dimple.
拉伸断口为韧窝和准解理混合断裂。
4.
The steel trea-ted with this pruccss shows a fractograph with quasi-cleavage and dimple。
钢的断口为准解理十韧窝属于韧性断裂。
5.
The fatigue fracture of test alloys has mixed-rupture characteristics of quasi-cleavage and dimples.
合金的疲劳断口呈现出准解理与韧窝断裂的混合特征。
6.
Fracture measurements show that the mode attributed to cleavage fracture.
断口实验结果表明,接头断裂模式为解理断裂。
7.
Application of physical fracture criteria to high speed cutting
物理断裂准则应用于高速切削的研究
8.
The fracture of composites assumes toughness dimple.
复合材料的拉伸断口为解理与韧窝混合断裂.
9.
Study on Mechanism of Ice-cover Breakup and Criterion for Onset of River-ice Breakup
开河期冰盖体断裂机理及开河判别准则研究
10.
Theoretical and Experimental Research on Choosing Criterion and Critical Value of Ductile Fracture
韧性断裂准则与阀值选取的理论及试验研究
11.
Analysis on Mechanism of Cleavage Fracture in a Low Alloyed Steel at Different Low Temperature
低合金钢在不同低温下解理断裂机理的研究
12.
Scanning electron microscope examination shows that the fractured surfaceschanges from the quasi-cleavage type to the cleavage type.
断口的扫描电子金相从准解理型过渡到解理型。
13.
Semi-analytical Finite Element Method for Quasi-brittle Material Fracture Analysis Based on Cohesive Force Model;
粘聚力模型下准脆性材料断裂分析的半解析有限元法
14.
Damage and Cleavage Study on Low Alloy Steel of Pressure Vessel;
压力容器用低合金钢的损伤与解理断裂研究
15.
Begging the Solution of Some Theorical Problems In Fracture Mechanics with Complex Functions;
用复变函数方法求解断裂力学的几个理论问题
16.
Integrated study for processing and interpretation in SG fault zone JH Depression
JH凹陷SG复杂断裂带处理解释一体化综合研究
17.
Fracture surfaces show predominant cleavage river pattern with a small quantity of dimples in the core.
硅钢断口边缘呈现解理断裂的“河流花样”,心部存在少量的韧窝。
18.
In this paper a mixed mode fracture criteria wasestablished which based on the Yu's unified strength theory from the commonness ofboth theory.
基于二者之间的共性，建立了一个基于统一强度理论的复合型裂纹断裂准则。