1) Slag resistance
抗渣性
1.
Slag resistance of Al_2O_3-spinel-SiC-C based castable;
Al_2O_3-MA-SiC-C质浇注料的抗渣性能
2.
Effect of matrix composition on slag resistance of alumina-magnesia castable;
基质组成对铝镁浇注料抗渣性能的影响
2) Slag resistance
抗渣性能
1.
Slag resistance of MgO-SiC-C composite;
MgO-SiC-C材料的抗渣性能研究
2.
The slag resistance of magnesia castable without Sialon and with 5% bauxite-based β-Sialon was studied by revolution dipping meth-od at 1 600℃ for 10,15,20 and 25 minutes.
采用中频感应炉进行旋转浸渍法抗渣实验,研究了未加入和加入5%矾土基β-Sialon镁质浇注料在1600℃不同浸渍时间(分别为10,15,20,25min)条件下的抗渣性能。
3.
The influence of Al2O3-SiO2 gel powder addition on permanent linear change,apparent porosity,cold crushing strength and slag resistance of Al2O3-MgO based castable was studied.
以电熔白刚玉和电熔镁砂为原料,以铝硅凝胶粉为结合剂制备Al2O3-MgO浇注料,研究铝硅凝胶粉加入量对Al2O3-MgO质浇注料线变化率、显气孔率、耐压强度和高温抗渣性能的影响。
4) Slag resistance
抗渣侵蚀性
1.
The results of slag resistance test show that the slag resistance of the specimen with TiN is better than the specimen without additive.
TiN提高镁碳砖抗渣侵蚀性的主要原因是:反应层中TiN的氧化产物TiO2与渣中的CaO反应生成熔点1970℃的CaTiO3;脱碳层中TiN氧化后形成的TiO2与C、CaO、MgO反应生成CaTiO3、2MgO。
5) slag,resistance,slagging resistance
抗渣性<抗熔渣侵蚀能力>
补充资料:抗渣性
分子式:
CAS号:
性质:耐火材料在高温下抵抗熔渣侵蚀的能力。熔渣侵蚀破坏耐火材料的机理十分复杂,一般包括有浸透、溶解和熔体冲刷等物理化学作用。抗渣性的表示方法可用熔渣侵蚀量mm或%表示。熔渣侵蚀是耐火材料在使用过程中最常见的一种损坏形式。耐火材料抗渣性的优劣主要与其自身的化学成分、矿物组成和组织结构等有关,还与熔渣的性质及其相互作用的条件(如温度、时间、流速等)有关。抗渣性是评价耐火材料的重要指标之一。
CAS号:
性质:耐火材料在高温下抵抗熔渣侵蚀的能力。熔渣侵蚀破坏耐火材料的机理十分复杂,一般包括有浸透、溶解和熔体冲刷等物理化学作用。抗渣性的表示方法可用熔渣侵蚀量mm或%表示。熔渣侵蚀是耐火材料在使用过程中最常见的一种损坏形式。耐火材料抗渣性的优劣主要与其自身的化学成分、矿物组成和组织结构等有关,还与熔渣的性质及其相互作用的条件(如温度、时间、流速等)有关。抗渣性是评价耐火材料的重要指标之一。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。