2) desulfuring ratio
固硫率
1.
CaO has higher desulfuring ratio when w (Ca) / w (S) is larger than 1∶1.
研究了氧化钙在煤燃烧过程中的固硫性能 ,讨论了燃煤的硫的质量分数、温度、钙硫比、稀土化合物对氧化钙固硫性能的影响·结果表明 ,随着煤中硫的质量分数的增加 ,氧化钙的有效利用率增加 ,钙硫比大于 1∶1时固硫效果比较好 ,氧化钙的最佳固硫温度约 90 0℃·随着煤粉和氧化钙的不断细化 ,氧化钙有效利用率也增加·在温度为 90 0℃ ,钙硫比为 1∶1时 ,最大固硫率约为70 % ,稀土化合物的添加 ,更有效地提高了氧化钙的利用率 ,可提高氧化钙的固硫率约 10 % ,且使固硫温度提高约 15 0℃
2.
The experimental results Showed that the desulfuring ratio of CaO increased with increasing of sulfur content of coal.
实验结果表明:随着煤中硫含量的增加,氧化钙的固硫率增大;氧化钙的固硫率在最佳固硫温度以下随温度升高而增大,超过最佳固硫温度则随温度升高而下降;氧化钙的最佳固硫温度约900℃;钙硫比大于1:1时固硫效果比较好,最大固硫率可达约72%;草酸铈和草酸镧的添加,更有效地提高了氧化钙的利用率,可提高氧化钙的固硫率约10%,且使固硫温度提高约100℃。
3) sulfur-fixing rate
固硫率
1.
Sulfur-fixing combustion experiments of coal water slurry with different sulfur contents were done and the results show that the sulfur-fixing rate of coal water slurry combustion is 9% higher than that of pulverized coal,sulfur-fixing capability of Ca(OH)2 is higher than CaCO3,formulated fixing agents based on Ca is prior to single component.
进行了不同含硫量煤制备脱硫型水煤浆燃烧固硫的试验研究,结果表明:在相同Ca/S值下,水煤浆燃烧固硫率比煤粉高9%左右,Ca(OH)2的固硫能力比CaCO3高,钙基固硫剂复配的固硫效果比单一使用某一类固硫剂要好。
2.
The sulfur-fixing rate of sulphoaluminate can be higher than 39%, CO_2 can o.
试验结果表明,温度是影响硫铝酸钙分解的主要因素;在1 300~1 500℃下, 降低氧气体积分数和增加二氧化碳体积分数可以不同程度地抑制在高温下形成的硫铝酸钙的分解,硫铝酸钙固硫率能够达到 39%以上;在1 400~1 500℃下,二氧化碳对高温下硫铝酸钙分解的抑制作用尤为显著。
4) sulfur-fixing rate at high temperature
高温固硫率
5) desulphurization
固硫
1.
Activity evaluation of fluidized bed combustion coal ash/slag with desulphurization;
流化床燃煤固硫灰渣活性评定方法
2.
One of the most important aims of this paper is to study the mineralogical characteristics of vermiculite from vermiculite mill gangue and apply this mineral to the desulphurization and dust clearing additives during coal combustion.
利用碳酸钙为固硫剂、膨润土为粘结剂、蛭石尾砂为膨胀添加剂对肥城烟煤进行高温燃煤固硫实验。
3.
The desulphurization characteristics of industry alkaline wastes and limestone were studied by means of flue gas analyzer and the high temperature tube reactor.
利用高温管式炉和烟气分析仪对4种工业碱基废弃物和1种石灰石固硫过程进行了试验研究,并利用压汞仪和X-射线衍射仪对废弃物的孔结构和固硫产物进行了研究。
6) sulfur fixation
固硫
1.
Study on sulfur fixation technology of coal briquette for civilian use;
民用型煤的固硫技术研究
2.
Research on sulfur fixation of calcium carbonate by automatic sulfur analyzer with coulometry;
利用库仑法测硫仪测试碳酸钙固硫效果的试验研究
3.
Catalysis mechanism of nano-additive on combustion and sulfur fixation;
纳米助燃固硫添加剂的催化作用机理
补充资料：固色率
分子式：
CAS号：
性质：活性染料与纤维发生化学结合的定量表示方式。其计算基准有二：(1)以染色时所用的染料总量为基准，固色率表示在纤维上结合的染料量与所用染料总量之比；(2)以固色前织物上的染料量为基准，表示固色后单位质量织物上的染料结合量与固色前单位质量织物上染料量之比。后一种计算法可用于分散染料对聚酯纤维的染色。
CAS号：
性质：活性染料与纤维发生化学结合的定量表示方式。其计算基准有二：(1)以染色时所用的染料总量为基准，固色率表示在纤维上结合的染料量与所用染料总量之比；(2)以固色前织物上的染料量为基准，表示固色后单位质量织物上的染料结合量与固色前单位质量织物上染料量之比。后一种计算法可用于分散染料对聚酯纤维的染色。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条