1) copper preplating
预镀铜
1.
An alkaline cyanide-free copper plating technology suitable for copper preplating on iron and steel substrates and for directly thick copper plating was established through tests of properties of plating bath and the coatings.
通过对碱性无氰镀铜工艺、镀液及镀层性能研究,得到该工艺可作为钢铁基体的预镀铜,也可直接用于镀厚铜,镀层与基体的结合力良好,结晶细致,光亮。
2) strike copper plating
预镀铜
1.
Non-cyanide alkaline strike copper plating process for zinc alloy die-castings;
锌合金压铸件无氰碱性预镀铜工艺
2.
Rinsing with tap water was popularly adopted between the procedures of strike copper plating and bright sulphate copper plating for copper alloy glasses.
铜合金眼镜架经预镀铜和光亮酸铜工艺处理,工序间普遍采用自来水水洗。
3) pre-plated copper
预镀铜
1.
Some experiments have been made to study the influence of the pre-plated copper on binding performance and corrosion resistance of mechanical zinc-plated layers.
研究了预镀铜对机械镀锌层的结合性能和耐腐蚀性能的影响。
2.
The process of replacement zinc plating,pre-plated copper and sulfate copper plating before electroplating is expounded.
介绍铜包铝丝、铜包铝镁合金丝的特点和用途,说明用电镀方法生产铜包铝丝、铜包铝镁合金丝的工艺过程及工艺特点,对电镀前的置换镀锌、预镀铜、加厚镀铜工艺进行详细论述,给出镀液、添加剂等的配制及维护方法。
4) cyanide pre-plating copper
氰化预镀铜
5) pre-coating copper without cyanogens
无氰预镀铜
6) ultrasonic-aid pre-plated copper
超声波预镀铜
1.
An ultrasonic-aid pre-plated copper as a base layer was applied in NdFeB permanent magnet.
对于NdFeB烧结永磁体,前处理后先超声波预镀铜,然后在pH=7、温度70℃的中性镀液中先施镀40min,再将镀液调至pH=5。
补充资料：镀铜
镀铜
copper coating
dUtong镀铜(eopper eoating)在酸洗后的盘条(线坯)表面镀覆一层铜，以作为拉丝时的润滑载体。以铜层作润滑载体主要用在拉拔轮胎钢丝与气体保护焊丝等特殊场合，这时铜层除用作润滑载体外，可提高轮胎钢丝同橡胶的结合力和焊丝的导电性。此外也用于弹妥钢丝等的生产中，以改善拉拔时的润滑性能及产品的表面质量。 镀铜操作时，把盘条浸入加有一定硫酸和骨胶的硫酸铜溶液中。根据电位序，铁能置换铜: Fe+CuZ+-今Cu+FeZ+并很快发生下列反应和完成镀铜过程 Fe+CuSO;一FeSO‘+Cu专硫酸铜是溶液的主要镀剂，提供铜离子的来源，浓度通常控制在60一7馆/L。浓度过低，将延长镀铜时间且不易获得所需厚度的镀层;浓度过高，则铜的沉积速度过快，导致铜结晶迅速长大，使镀层疏松、粗糙，影响与基体的结合。硫酸的主要作用是活化盘条表面，使铜层能与基体牢固结合。骨胶有促使铜与基体粘合的作用，并使铜层结晶细密。镀铜时溶液温度必须控制在簇25℃，温度较低时，镀层光亮致密，但生产率低。温度过高时，则镀层厚，且粗糙、疏松、附着力差。溶液中Fe2+离子过多会恶化镀层质量。镀铜过程约在1一2而n内完成。 (韩观昌)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条