1) sticking breakout
黏结漏钢
1.
Causes and countermeasures for sticking breakout in wide slab caster;
超宽板坯连铸机黏结漏钢原因及预防措施
2.
Causes and countermeasures for sticking breakout of fast SEN changing;
快换浸入式水口发生黏结漏钢原因和预防措施
2) breakout by sticking
粘结漏钢
1.
4 slab caster of JISCO,the reasons of breakout by sticking of 50# steel slab were analyzed systematically.
本文结合酒泉钢铁公司4#板坯生产实际,系统分析了50#钢粘结漏钢的原因,从保护渣、结晶器、冷却水以及工艺操作等方面有针对性地制定了措施,杜绝了粘结漏钢事故,稳定了生产。
2.
Analysis consider that the reason of breakout by sticking is bad capability of the powder,such as lower depth of liquid powder,less consumption and low proportion of glass phase in the powder.
分析认为,济钢大板坯连铸机出现粘结漏钢的原因是保护渣的性能不良,其中液渣层厚度、渣耗量及玻璃相比例偏低,以及结晶器液面波动,拉速提升过快等。
3.
It is shown that the breakout by sticking is caused by low temperature of molten steel and high withdrawal speed and illogicality capability of protecting slags.
通过统计分析板坯连铸生产中出现的漏钢事故,认为钢水温度低、拉速快和保护渣理化性能不合理易导致粘结漏钢;对弧不良、钢水温度高、拉速快是造成裂纹漏钢的主要原因;开浇和接头漏钢主要是中间包上水口和塞棒烘烤效果不好及出苗时间不足造成的。
3) sticking breakout
粘结漏钢
1.
Optimization for flux of high-carbon steel #45 is put forward through studying casting characteristic of high-carbon steel and analyzing the reasons of sticking breakout.
通过研究高碳钢连铸特点,分析了高碳钢板坯连铸粘结漏钢的原因,提出了板坯连铸45#高碳钢保护渣优化设计思路。
2.
This article introduces the mechanism,main characteristic of sticking breakout.
介绍了大板坯连铸粘结漏钢的发生机理和和主要特点;结合邯钢三炼钢厂生产实践,分析了工艺、操作和设备等因素对粘结漏钢的影响;提出了降低粘结漏钢次数的主要措施。
4) breakout of steel
粘结性漏钢
1.
In the paper the viscous breakout of steel is analyzed and summarized.
分析了宝钢近年来粘结性漏钢发生的情况,总结出防止产生粘结性漏钢的三大要素:控制液面波动、把握保护渣性状规范加渣操作、监视拔热量。
5) Bonded Steel Plate
黏钢
1.
Contact element analysis about the interface stresses strengthened by Bonded Steel Plates;
接触单元分析黏钢加固的界面应力研究
6) funnel viscosity
漏斗黏度
1.
To certain extent,the funnel viscosity is an indicator of the quality of slurries.
泥浆漏斗黏度是泥浆特性的一个重要指标,泥浆漏斗黏度对盾构掘进效果有重要影响。