1) Cu-Ti composite diffusion coating
Cu-Ti复合渗镀
1.
Cu-Ti composite diffusion coating for joining Si_3N_4 ceramic to metal;
以Cu-Ti复合渗镀为先导的Si_3N_4陶瓷/金属钎焊连接
2) Ni-Ti composite diffusion coating
Ni-Ti复合渗镀
3) Ti-Ni composite plating
Ti-Ni复合镀
4) composite depositing
复合渗镀
1.
Based on the composite depositing technology by the arc-added glow discharge, the composite target was used to deposit Cu and Ti alloy on the Al_2O_3 ceramics surface, realizing the surface alloying of Al_2O_3 ceramics.
基于加弧辉光复合渗镀技术,采用自行研制的复合靶对Al2 O3陶瓷表面进行Cu、Ti复合渗镀,实现了Al2 O3陶瓷表面合金化。
2.
Based on the composite depositing technology by the arc-added glow discharge, the composite target was used to deposit Cu and Ti alloy on the Al_2O_3 ceramics surface, realizing the surface alloying of A1_2O_3 ceramics.
基于加弧辉光复合渗镀技术,采用自行研制的复合靶对Al_2O_3陶瓷表面进行Cu、Ti复合渗镀,实现了Al_O_3陶瓷表面合金化。
5) Ti/Cu/Ti composite interlayer
Ti/Cu/Ti复合中间层
1.
Microstructure in diffusion bonded TiC-Al_2O_3/W18Cr4V joint with Ti/Cu/Ti composite interlayer;
Ti/Cu/Ti复合中间层扩散连接TiC-Al_2O_3/W18Cr4V接头组织分析
6) Al/Ti coatings
Al/Ti复合镀层
1.
The thermal stress for Al/Ti coatings on uranium substrate was analyzed by using a thermal elastic plastic finite element method (FEM).
对铀表面Al/Ti复合镀层的热应力进行了热弹塑性有限元分析,表明Ti镀层内为压应力,Al镀层内为拉应力,并达到铝的屈服强度,靠近试样侧边,存在边缘效应引起的应力分布不均匀性,离试样侧边2倍镀层厚度处,不均匀性逐渐消失,试样侧边U-Al界面剪切应力大于中部区域。
补充资料：渗镀
分子式：
CAS号：
性质：在高温下将气态、固态或熔化状态的欲渗镀的物质（金属或非金属元素）通过扩散作用从被渗镀的金属的表面渗入内部以形成表层合金镀层的一种表面处理的方法。所形成的镀层称为渗镀层。用于提高抗氧化性（抗蚀性）、耐热性和耐磨性等。渗镀层与基体金属之间是靠形成合金来结合的，因而结合牢固，镀层不易脱落。以渗镀物质的状态分为固渗、液渗和气渗；以联合用其他涂层方法来分，有粉末包渗、热浸法渗、电泳渗、料浆参或膏剂渗、喷镀渗、电镀渗和化学镀渗等；以渗入元素的名称和种类分又有渗铝、渗硅、渗铬等，以及二元共渗、多元共渗等。镀层有抗高温氧化、耐腐蚀、耐磨损等优良性能。