1) cooling cracks the susceptible index number
冷裂纹敏感指数
1.
It takes X60's steel as the instance,preheating temperature of pipeline steel has been got by carbon equivalent and cooling cracks the susceptible index number calculation.
以X60钢为例,通过碳当量和冷裂纹敏感指数的计算,确定了管线钢的预热温度,并与斜Y坡口焊接裂纹试验的结果进行了比较,经过分析推荐了适用于管线钢的预热温度计算公式。
2) cold crack sensitivity
冷裂纹敏感性
1.
50 mm WNQ570 steel,a new type of steel for railway bridge,has been carrying on the experiments of cold crack sensitivity through CJ607Q welding rod and submerged WS03 arc welding wire and SJ101Q welding flux.
采用CJ607Q焊条和WS03埋弧焊丝与SJ101Q焊剂对铁路桥梁用WNQ570钢50 mm厚钢板进行了焊接冷裂纹敏感性试验。
3) crack sensitivity coefficient
裂纹敏感系数
1.
The computer numerical simulation technique is used to simulate and analyze the temperature field, the thermal stress and the crack sensitivity coefficient of the ingot mold FZ25t during the solidification period of the ingot.
针对大型灰铸铁扁型钢锭模早期裂纹报废问题，采用计算机模拟计算技术对ＦＺ２５ｔ钢锭模使用过程的温度场、热应力和裂纹敏感系数的变化过程进行了数值计算分析，并优化了结构设计。
4) cold cracking susceptibity coefficient
冷裂敏感系数
5) Welding Cold Crack Sensitivity
焊接冷裂纹敏感性
1.
Trial Production of Micro Alloying Low Welding Cold Crack Sensitivity Steel WDB620;
非调质低焊接冷裂纹敏感性钢WDB620的试制
6) cracking susceptibility
裂纹敏感性
1.
Current EBW experiments on IC10 guide blade which is being researched in China have shown that the EBW has an obvious cracking susceptibility.
本文介绍了该合金的真空钎焊、TLP扩散焊的研究进展情况,重点分析了我国目前在研的IC10合金导向叶片产生明显电子束焊接裂纹敏感性的原因,并指出了改善电子束焊接工艺参数、填丝合金化和焊后热处理等解决方案。
2.
These help to improve the hot ductility and to alleviate the cracking susceptibility of the slab.
s-1的冷却速度,使铸坯在出结晶器后表面温度下降到A3温度以下,得到的表层组织均匀,晶界无膜状先共析铁素体,微合金元素析出物在晶内分布均匀,有利于提高铸坯热塑性及降低裂纹敏感性。
补充资料：冷裂纹
分子式：
CAS号：
性质：焊接接头冷至较低温度下，大约在钢的马氏体转变温度附近，由于拘束应力、淬硬组织和氢的作用下产生的裂纹属冷裂纹。冷裂纹主要发生在低合金钢、中合金钢和高碳钢的热影响区。
CAS号：
性质：焊接接头冷至较低温度下，大约在钢的马氏体转变温度附近，由于拘束应力、淬硬组织和氢的作用下产生的裂纹属冷裂纹。冷裂纹主要发生在低合金钢、中合金钢和高碳钢的热影响区。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。