1) semi-solid melt
半固态熔体
1.
Then according to its particular features, the key techniques were presented which contained semi-solid melt quick-preparation, quantitative pouring, gating system design and the optimization of processing parameter and was considered as the main factor that controlled the performance of workpiece.
分析了半固态合金熔体直接压铸技术的特点及优势后指出,控制半固态压铸件性能的关键性技术是半固态熔体快速制备技术、定量浇注、浇注系统设计和工艺参数的优化设计。
2) semi-solid remelting
半固态重熔
1.
8Mg alloy are investigated in semi-solid remelting condition.
试验结果表明 :半固态重熔时 ,α晶体的形态的演变过程按液相量和成份的变化以及α晶体的形态变化分为 3个阶段 :第一阶段为液相量的增加阶段 ;第二阶段为液相成份向平衡亚共晶成份转化阶段 ;第三阶段为液相达平衡亚共晶成份以后的阶段 ;在第一和第二阶段 ,α晶体以碰撞合并方式长大 ,第三阶段按Ostward方式长大。
3) Welding in Vacuum
真空半固态熔覆技术
4) translucent solid polymers
半透明固态聚体
5) solid zone melting
固态区熔
6) solid solution
固熔体
1.
84×10 -3 S/cm,and the study results show that solid solution of inorganic salts has important effect on the conductivity of SPE.
用无机盐和脲制成固熔体 ,加入 PEG,PVA等高分子物质制备新型的“Polymer- in- Salt”。
2.
The results show that,when adding Pd into Ni/Si,thermal annealing leads to formation of a solid solution Ni 1-x Pd x Si layer with better thermal stability than NiSi.
结果表明 ,加入 Pd层后 ,退火形成 Ni1 - x Pdx Si固熔体 ,该固熔体比 Ni Si的热稳定性好 ,使得 Ni Si向 Ni Si2 的转变温度升高 。
补充资料：半熔体纺丝
分子式：
分子量：
CAS号：
性质：见凝胶纺丝法。
分子量：
CAS号：
性质：见凝胶纺丝法。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条