1) hardness
膜层硬度
1.
The thickness and hardness of the resulting ceramic coatings formed at fixed pulse width and frequency but varied duration and oxidation power were measured, and the changing tendencies of the thickness and hardness of the ceramic coatings with th.
为了说明微弧氧化过程中能量的实质作用,引入氧化功率概念,以LY12铝合金为样品,采用脉冲电源,在一定的脉宽、频率条件下,改变微弧氧化时间、微弧氧化功率等参数,获得相应的铝陶瓷膜,通过对相关样品进行膜层厚度、膜层硬度测量,得到一系列数据,研究并找出其变化规律。
2) coating
膜层
1.
The micro-arc oxidation ceramic coatings were formed on the titanium alloy surface by micro-arc oxidation in Na_2SiO_3 solution using an AC power.
结果表明:陶瓷膜表面的微孔直径、粗糙度随微弧氧化频率的增大而减小;陶瓷膜/环氧树脂的结合强度随频率的增加先是快速上升,当频率增加至400Hz时,膜层的结合强度达到最高值56。
2.
A self-made impact tester with low energy was used to evaluate the adhesion,cohesion and toughness etc of physical vapor deposited(PVD) CrMo and TiAlN coatings.
利用自行研制的小能量多冲试验装置,对物理气相沉积(PVD)方法制备的CrMo合金膜和TiA lN陶瓷膜的结合强度、韧性、内聚强度等机械性能进行综合评价;探讨了膜层性质、冲头几何形状、基材硬度等因素对PVD膜层在小能量多冲条件下失效行为的影响规律;比较了膜层在承受动态多冲与静态压入载荷条件下失效行为的异同;分析了膜层在小能量多冲条件下的失效机制。
3.
This paper discuss on the choice of the substrates,coating materials and coating systems of the mirrors of the resonant cavity of high power CO2 laser.
本文讨论了大功率ＣＯ２激光器腔镜基片、膜料和膜系的选择，给出了常用膜料可构成的λ／４膜系反射率，指出了一种在输出镜上获得任意中间反射率的方法，介绍了膜层制作工艺。
3) Film
膜层
1.
The result indicated that the reactions producing the phases in the coating were thermodynamically possible, and the formation of the MAO film was not a typical nucleation and growth process.
膜层是在不断击穿、生成、烧结、排泄堆积等过程中生长起来的,而且在反应过程中,膜层的生成是由反应电压、电流、电解液体系、pH值等各种工艺参数所控制的。
2.
The growth process of micro-arc oxidation film on magnesium alloys and the influencing factors were discussed.
对镁合金微弧氧化膜层的形成过程以及形成过程中的工艺影响因素做进一步的探讨,得出微弧氧化膜层的形成是一种亚单层生长模型,它是“成膜→击穿→熔化→烧结→再成膜……”的多次循环过程。
3.
Physical,chemical and mechanical characteristics of metal electrodepositing film depend on its structure and organization,which are influenced by many factors.
电沉积金属膜层的物理、化学性质以及力学性能与其组织结构密切相关 ,而沉积金属膜层的组织结构受诸多电沉积工艺条件的影响。
4) layer
膜层
1.
Single-layer and multilayer ZnO thin films are deposited by means of gas discharge active reaction evaporation through single and multiple depositions at relatively lower temperatures.
分析了不同膜层及热处理温度对ZnO薄膜压敏特性的影响机理。
5) ceramic coating
陶瓷膜层
1.
Formation mechanism of surface ceramic coating on aluminum alloy;
铝合金表面陶瓷膜层形成机理
2.
Ceramic coating was obtained by micro-arc oxidation on LY12 aluminum alloy in sodium silicate and sodium hydroxide electrolyte,and examined by SEM and TEM.
在硅酸钠和氢氧化钠电解液中利用微弧氧化技术在LY12铝合金表面生成陶瓷膜层。
3.
It is very important to research the effect of cathode voltage on the forming of ceramic coatings.
在交流条件下,采用硅酸钠电解液,通过调节不同的负向电压值,在ZAlSi12Cu2Mg1合金表面制得了微弧氧化陶瓷膜层。
6) coating growth
膜层生长
参考词条
补充资料：工程塑料硬度的检测--巴氏硬度计
HBa-1巴 氏 硬 度 计巴柯尔 (Barcol) 硬度 ( 简称巴氏硬度 ) 最早由美国 Barber-Colman 公司提出，是近代国际上广泛采用的一种硬度门 类，以特定压头在标准弹簧的压力作用下压入试样，以压痕的深浅表征试样的硬度。巴柯尔硬度计（巴氏硬度计）作为 专门测量玻璃钢制品、增强或非增强硬塑料、铝及铝合金、黄铜、紫铜等较软金属硬度的专用检测工具 （ 特别 适用于玻璃钢制品 ），已被大多数国家或国际组织认可。美国材料试验协会（ ASTM ）、日本工业规范（ JIS ）、中国等国家相继制定 《用巴柯尔硬度计测量玻璃钢（ GRP ）硬度试验方法》,《纤维增强塑料巴氏（巴柯尔）硬度试验方法》GB/T3854-1983 的国家标准。因此，巴柯尔硬度计是各生产单位、计量部门在质量认证、质量监控、计量测试等方面首选的专用检测仪器。 无锡市计量科学研究所，是我国制定巴柯尔硬度检定标准的主要参与者、巴柯尔硬度最高标准器的拥有者和国产第一台巴柯尔硬度计的研制和生产单位，也是国家实验室认证的巴柯尔硬度计专业检测机构。经过二十多年的不断完善，本所生产的 H Ba 系列巴柯尔硬度计的各项性能和技术指标完全与美国 Barber-colman 公司 GYZJ 系列硬度计相媲美 。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。