1) Co-Ni-Al_2O_3
Co-Ni-Al2O3
1.
It illustrates from the examined results of SEM, AFM and XRD that surface morphology and microstructure of Co-Ni-Al_2O_3 coatings appear to be mainly influenced by variations in cobalt content.
通过SEM,AFM以及XRD等分析测试方法,研究了Co-Ni-Al2O3复合镀层的表面形貌和微观晶体结构。
2) Ni(Co)Mo(W)/Al2O3 catalysts
Ni(Co)Mo(W)/Al2O3催化剂
3) Al2O3/Ni-Co nanocomposite
Al2O3/Ni-Co纳米复合材料
1.
Al2O3/Ni-Co nanocomposite containing various Al2O3 particles were produced by pulse electrodeposition.
本文采用脉冲电沉积方法制备了含不同Al2O3颗粒的Al2O3/Ni-Co纳米复合材料,研究添加剂、Al2O3颗粒对材料组织、力学性能和热稳定性的影响,通过超塑单向拉伸实验研究Al2O3/Ni-Co纳米复合材料的超塑性。
4) Ni-Al_(2)O_(3)
Ni-Al2O3
5) Al_2O_3-TiC-Co
Al2O3-TiC-Co
1.
Al_2O_3-Co+TiC-Co composite powder prepared by electroless plating method was sintered into the ultra-toughen Al_2O_3-TiC-Co cermet by hot pressing technique.
热压烧结化学镀法获得的Al2O3-Co+TiC-Co复合粉体制备超韧Al2O3-TiC-Co复合陶瓷。
6) Co-Cr/Al_(2)O_(3)
Co-Cr/Al2O3
补充资料:Ni-Al microwave ferrite
分子式:Ni-Al
CAS号:
性质:又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上,用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%,磁性出现反常现象,这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035~0.145T,随铝量换量的增加而降低。居里温度155~440℃。铁磁共振线宽18.0~44.0kA/m(9kHz)。介电常数8.2~9.5。介质损耗角正切值(3~50)×10-4。采用电子陶瓷工艺,热压烧结或氮气氛烧结。适于制作高功率器件。
CAS号:
性质:又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上,用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%,磁性出现反常现象,这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035~0.145T,随铝量换量的增加而降低。居里温度155~440℃。铁磁共振线宽18.0~44.0kA/m(9kHz)。介电常数8.2~9.5。介质损耗角正切值(3~50)×10-4。采用电子陶瓷工艺,热压烧结或氮气氛烧结。适于制作高功率器件。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条