1) casting Fe_3Al alloy
铸造Fe3Al合金
2) Fe_3Al alloy
Fe3Al合金
1.
Fe_3Al alloy is an excellent heat resistance engineering material.
Fe3Al合金是优秀的耐热工程材料,在测定合金流动性工艺参数的基础上,用热力学观点分析了主要添加元素Al对合金流动性的影响规律。
2.
According to the test results of the casting technology properties of Fe_3Al alloy, the technological design principle of the castings was established.
在测定Fe3Al合金铸造工艺参数的基础上,制定出了相应的铸造工艺设计原则。
3) Fe3Al-based alloy
Fe3Al基合金
1.
Current research status of welding of Fe3Al-based alloys;
Fe3Al基合金焊接问题的研究现状
4) Fe3Al alloy
Fe3Al合金
5) Cast Alloy
铸造合金
1.
On the basis of orthogonal experiment, the effect of Mg content and heat treatment on mechanical properties of near eutectic Al Si cast alloys modified with Sr has been investigated.
以正交试验为基础 ,通过调整Mg含量和热处理工艺 ,分析它们对Sr变质近共晶Al Si铸造合金力学性能的影响。
2.
The effect of carbon content on element segregation and corrosion resistance of the cast alloy Fe 30Ni 20Cr 6Mo has been investigated.
研究了Ｆｅ－３０Ｎｉ－２０Ｃｒ－６Ｍｏ铸造合金中微量元素Ｃ对合金元素偏析和耐蚀性的影响。
3.
Effect of microstructure and element distribution of an iron base cast alloy Cr30Nil7Mo2Cu solidified at different rates upon the erosion-corrosion behaviour in flowing suspension of solid particles in strong acidic medium has been investigated by metallograph, XRD, EPMA and hardness tests.
用扫描电镜、Ｘ射线衍射、电子探针等手段测定及分析了Ｆｅ基铸造合金Ｃｒ３０Ｎｉ１７Ｍｏ２Ｃｕ以不同速度凝固后的显微组织和主要合金元素分布，在含固相颗粒的强酸性双相流介质中测定了冲刷腐蚀性能。
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜