1) prevent slag from going into blast furnace
高炉防灌渣
2) blast furnace slag
高炉炉渣
1.
Alumina content in Nanjing Steel blast furnace slag is up to 19%,which results in worse slag fluidity,higher furnace operating temperature and higher silicon content of hot metal.
南京钢铁集团公司高炉炉渣中氧化铝含量高达19%,因此炉渣流动性变差,高炉被迫采用高温操作,铁水硅含量偏高,影响了高炉的强化。
2.
The measurementand systemat-ic study had been made on chemical components,mineral compositions,mineral structure,viscosity and melting tem-perature of the blast furnace slag.
试验选取生产现场的高炉炉渣作为基准原料,对现场高炉炉渣和高炉初渣的化学成分、矿物组成、矿物结构以及粘度和熔化性温度进行了测定和系统研究。
3.
INBA is a new type of blast furnace slag processing technology,can be converted to high - grade blast furnace slag cement materials,the recycling of slag implementation.
INBA法是一种新型高炉炉渣处理技术,可以将高炉废渣转为高品位的水泥原材料,实现炉渣的再生利用。
3) BF slag
高炉炉渣
1.
The metallurgic characteristic of Tanggang BF slag was researched in laboratory onthe basis of the current production parameters in the paper.
本文以唐钢高炉生产条件为基础,对唐钢高炉炉渣的冶金性能进行了实验室研究,分析CaO/SiO_2、Al_2O_3、MgO 这三个因素对炉渣的冶金性能产生的重要影响,建立其冶金性能的数学模型,并得出炉渣在高Al2O3条件下合理的造渣制度。
4) blast furnace slag
高炉炉渣<冶>
5) blast furnace slag
高炉矿渣
1.
A large quantity of blast furnace slag discharged in Laiwu Steel Company causes serious environmental pollution.
莱钢每年排放大量的高炉矿渣造成了严重的环境污染,利用高炉矿渣生产微晶玻璃受到国内外的广泛关注。
2.
Replacement of pebbles with blast furnace slag for roadbed and road base cannot only solve the problem of transportation and construction cost,but can solve the problem of pollutions caused by abandoned blast furnace slag,which is significant for the alleviating material shortage,increasing the value of slag,comprehensive utilization and protection of the ecological environment.
高炉矿渣代替碎(卵)石作为公路路基、路面基层材料既可解决材料运距长、建设成本高的问题,又能解决被废弃高炉矿渣占用大量土地资源并对环境造成严重污染的问题,对缓解路用材料短缺,提高矿渣价值和综合利用率,以及保护生态环境等方面具有重大意义。
3.
In view of both the understanding of the double-interface sealing system and the basic analysis of the chemical and physical properties of blast furnace slag(BFS),a set of experimental facilities was developed for the simulation of interfacial bonding in cementing,and experimental evaluation was conducted on the performance of blast furnace slag cement system by bond strength simulation test.
基于对双界面封固系统的认识和对高炉矿渣物化特性的分析,研制了用于模拟固井界面胶结的试验装置,利用胶结强度模拟试验等方法评价了高炉矿渣水泥体系的性能。
6) slag
[英][slæɡ] [美][slæg]
高炉矿渣
1.
The flyash and slag, with standard sand as aggregate, were used as principal mat erials to prepare mineral polymer.
以粉煤灰,高炉矿渣为粉体原料,标准砂为骨料,采用振动成型方法,在蒸压釜中蒸压养护9h(养护温度为192℃),制备了矿物聚合材料。
2.
Glass-ceramic was made from the slag of Bao-Steel Corporation in Shanghai by body crystallization.
以宝钢高炉矿渣为原料整体析晶法制备矿渣微晶玻璃,通过DTA确定微晶玻璃的热处理制度,通过XRD确定玻璃的主晶相,利用SEM观察微晶玻璃的显微形貌,并对微晶玻璃的抗折强度进行测试。
补充资料：高炉泡沫渣
高炉泡沫渣
the foaming slag of blast furnace
一定值后会有大量气体以气泡形式分散于渣中使炉渣的体积膨胀‘这种炉渣即为泡沫渣，它是特殊矿冶炼高炉造渣的一个重要问题。泡沫渣的产生将造成高炉生产过程渣铁出不尽，料柱透气性恶化，风口易挂渣，给高炉炉况顺行和强化带来困难。当炉渣进入渣罐后由于其体积膨大使渣罐利用率降低，甚至从渣罐上部溢出，造成事故。泡沫渣的形成有两个条件，一是有大量的分散气体生成，二是炉渣性能使分散气体稳定存在，从而使渣中气体量不断增加。在钒铁磁铁矿的高炉冶炼中，高炉下部有较多的Feo、TIO:等氧化物从渣中还原，从而产生大量CO气体。同时，高钦型高炉渣表面吸附，富集的活性物质比普通渣高得多。表面活性物.的存在使液膜的表面私度比体积豁度高，从而阻碍了排气速度，延长了泡沫的寿命。表面活性物的存在又使炉渣表面张力大大下降，造成渣内分散气泡合并上浮困难，使气泡更稳定，从而形成泡沫渣。解决泡沫渣间题的办法是采用一切手段提高渣中“氧势”，抑制TIOZ还原，减少Ti(C、N)等胶质微粒的生成，也即减少表面吸附的活性物质量，从而阻止泡沫形成。goolu Paomozha高炉泡沫渣(the foaming、lag。f blast fur-nace)高炉冶炼钒钦磁铁矿时，炉渣中Tio。高达
说明：补充资料仅用于学习参考，请勿用于其它任何用途。