1) coating of silicon acid and rich zinc
硅酸富锌涂料
2) waterborne inorganic zinc silicate coating
水性无机硅酸富锌涂料
3) silicate zinc paint
硅酸锌涂料
1.
Since 60 s, riveted-welded steel beqams are replaced by bolted-welded ones in steel bridge manufacture in China To ensure the anti-slide coefficient of contact surface,we have developed this kind of an ti-slide, antirust, silicate zinc paint.
我国钢桥制造自60年代由铆焊粱改为栓焊梁，为保证栓接面一定的抗滑移摩擦系数，特研制了此防滑防锈硅酸锌涂料。
4) zinc-rich coatings
富锌涂料
1.
The paper introduced the characteristics of several zinc-rich coatings anti the method of zinc content measurement.
介绍了几种富锌涂料的特点及其锌含量的测定方法。
2.
This paper introduces new development trend of overseas zinc-rich coatings preparation with zinc flake instead of spherical zinc powder and discusses the anticorrosion mechanism of flake zinc-rich coatings film.
介绍了国外采用鳞片状锌粉取代球状锌粉研制富锌涂料发展的新趋势,对鳞片状锌基涂层抗蚀性能的机理进行了探讨,并从实际实验数据中得到了与理论分析相一致的结论,即鳞片状锌粉涂层在干膜含锌量降低的情况下,其抗蚀性能仍优于球状锌粉涂层,鳞片状富锌涂料是球状富锌涂料理想的换代产品。
3.
The formulation of high mole ratio potassium silicate zinc-rich coatings is given, which is compared to the similar products abroad in terms of its performance.
研究了不同硅溶胶、硅酸钾和烷氧基硅烷对高模数硅酸钾制备的影响 ;探讨了温度、时间和搅拌速度对高模数硅酸钾制备的影响 ;进行了高模数硅酸钾富锌涂料的配方实验 ,并与国外样品的性能进行了比较。
5) zinc-rich coating
富锌涂料
1.
Study on the curing mechanism of sodium silicate inorganic zinc-rich coating;
钠水玻璃富锌涂料固化机理的探讨
2.
The electrochemical behavior of the modified waterborne epoxy - polyurethane zinc - rich coatings with different amounts of zinc powder in 3 % NaCl solution was investigated using corrosion potential test and electrochemical impedance spectroscopy (EIS) , and compared with that of zinc-rich coating containing a small amount of aluminum powder and traditional epoxy zinc-rich coatings.
为制得环保且防腐蚀性能优异的富锌涂料,引入环氧树脂来改性水性聚氨酯,以水性环氧聚氨酯为基料制备富锌涂料,通过对其腐蚀电位和电化学阻抗谱(EIS)的测试分析,研究了添加不同含量锌粉的富锌涂层在3%NaCl溶液中的腐蚀电化学行为,并与添加少量铝粉的富锌涂料及传统富锌涂料进行了对比。
6) zinc silicate antirust paint
硅酸锌防锈涂料
补充资料：硅酸质类主层涂料
硅酸质主层涂料是以硅溶胶或水溶性硅酸盐和固化剂为主要粘结剂，分别加入高分子合成树脂乳液、助剂、填料、细骨料等混合而制成。硅酸质类主层涂料虽与水泥类主层涂料同属以sio2为骨架的材料，但其硬化机理和性质全然不同，所以使用时必须区别对待。
组成硅酸质主层涂料的水溶性硅酸盐可以是硅酸锂、硅酸钠、硅酸钾或其混合物，固化剂为在硅酸盐水溶液中能缓慢释放出氢离子的弱酸、强酸弱碱盐、酸性氧化物、两性氧化物、两性氢氧化物等。实际配制中用缩合磷酸铝为主要固化剂。高分子合成树脂乳液包括乙烯-乙酸乙烯乳液、苯丙乳液等。主要填料有碳酸钙、灰硅石粉、滑石粉、二氧化硅粉，细骨料为石英粉（80~100目）。增稠剂为高黏度甲基纤维素、羟乙基纤维素。另外还需加分散剂、稳定剂、防霉防腐剂等。
硅酸质主层涂料的特点是不会像水泥材料那样由于本身的原因产生粉化或泛白。硅溶胶为二氧化硅的胶体颗粒，其粒径比乳液粒径小，向基层渗透力强，所以附着性好，不会起皮脱落。但因是无机材料，故没有什么弹性，不能随基层的伸缩而变形，易造成开裂。该类主涂层使用较少。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。