1) Si-Ca-Ba-Al alloy
Si-Ca-Ba-Al合金
2) Si-Ca-Ba Alloy
SI-CA-BA合金
1.
The variation rules of deoxidation and inclusion modification in molten steel treated by Si-Ca-Ba alloys with different Ba and Ca contents were researched in laboratory.
在实验室条件下考察了不同钡、钙质量分数的Si-Ca-Ba合金对钢液脱氧和夹杂物变性作用的变化规律。
2.
The variation rules of deoxidation and metamorphic effect to inclusions in molten steel treated by Si-Ca-Ba alloys with different Ba and Ca contents were researched in laboratory.
在实验室条件下考察了不同Ba、Ca含量的Si-Ca-Ba合金对钢液脱氧和夹杂物变性作用的变化规律。
3) Si-Ca-Ba alloy melt
Si-Ca-Ba合金熔体
4) Si-Ca-Sr-Ba alloy
Si-Ca-Sr-Ba合金
5) Al-Si-Ca-Ba compound deoxidizer
Al-Si-Ca-Ba复合脱氧剂
6) Al-Ca alloy
Al-Ca合金
1.
In this paper, using CaO as starting material, the binary system of CaCl_2-CaF_2 as well as the ternary system BaF_2-CaF_2-CaCl_2 ternary as electrolyte, Al-Ca alloy was produced by molten salt electrolysis method.
本文以CaCl_2-CaF_2二元系和BaF_2-CaF_2-CaCl_2三元系为电解质,CaO为原料,熔盐电解制备Al-Ca合金,研究了熔盐物理化学性质,并考察了电解工艺参数。
2.
A new process for Al-Ca alloy preparation by molten salt electrolysis was investigated using sinking-mode aluminum liquid as cathode and a mixture of CaCl2-CaF2 as molten salt electrolyte.
研究了在CaCl2-CaF2纯钙盐体系中下沉式铝液槽结构熔盐电解法生产Al-Ca合金新工艺,采用连续脉冲-示波器法测定电解过程的反电动势,研究了在实验室条件下电解温度、电流密度、电解时间和极距对熔盐电解法制取铝钙合金的反电动势的影响。
补充资料：Al-Si cast aluminium alloy
分子式：
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。