1) carbon felt-carbon composites
碳毡/碳复合材料
2) carbon fiber felt copper composites
碳毡/铜复合材料
1.
The friction and wear properties of carbon fiber felt copper composites fabricated by electrodeposition were studied.
本文研究了用电沉积法制备的碳毡／铜复合材料的摩擦磨损特性。
3) carbon-felt reinforced carbon composites
碳毡增强碳复合材料
4) carbon/carbon composites
碳/碳复合材料
1.
Preparation of biomedical carbon/carbon composites and their bone tissue biocompatibility;
医用碳/碳复合材料的制备及骨组织相容性研究
2.
The effect of plasma spraying powers on hydroxyapatite coated on carbon/carbon composites;
喷涂功率对碳/碳复合材料表面羟基磷灰石涂层的影响
3.
Microstructural evolution of phenolic resin-based carbon/carbon composites during pyrolysis;
基于酚醛树脂的碳/碳复合材料在高温分解过程的微结构演变
5) carbon/carbon composite
碳/碳复合材料
1.
Study on application of carbon/carbon composites;
碳/碳复合材料的应用研究进展
2.
Promising candidate as the aircraft engine material-carbon/carbon composite;
潜在的航空发动机材料——碳/碳复合材料
3.
Oxidation mass loss rates of different samples at different temperature and time were studied,and relation of carbon felt density and oxidation behavior of carbon/carbon composite was studied.
采用自加热化学液相沉积法制备碳/碳复合材料。
6) C/C composites
碳/碳复合材料
1.
Study on the oxidation mechanism of the coated C/C composites;
涂层碳/碳复合材料氧化机理的研究
2.
Cf/C composites were bonded to C/C composites with Cu based brazing filler metal at 1 000 ℃-1 100 ℃ in vacuum.
用铜基活性钎料对碳/碳复合材料进行了真空钎焊,并对接头的微观组织、形成机理和接头强度进行了试验研究。
3.
The recent advancement of the oxidation protective coatings of C/C composites in China was reviewed.
重点阐述国内近几年来碳/碳复合材料抗氧化涂层的研究新进展,总结碳/碳复合材料高温抗氧化涂层制备新工艺和对已有工艺的改进方法,结合碳/碳复合材料的应用背景对抗氧化涂层的发展趋势进行展望。
补充资料：碳毡
分子式：
CAS号：
性质：碳纤维制成的毡，简称碳毡。以聚丙烯腈基碳毡为例，定积重量500g/m2和1000g/m2，纵向和横向强度(N/mm2)各为0.12，0.16和0.10，0.12，断裂伸长各为3％、4％和18％、16％，电阻率(Ω·mm)各为4～6，3.5～5.5和7～9，6～8，导热系数各为0.06W/(m·K)(25℃)，比表面积均>1.5m2/g，灰分皆小于0.3％，含硫量皆<0.03％。制法有：(1)碳短丝气流成网后针刺；(2)预氧丝毡碳化；(3)聚丙烯腈纤维毡预氧化和碳化。用作真空炉和惰性气体炉绝热材料、热的气体或液体和熔融金属滤材、燃料电池多孔电极、催化剂载体、耐腐蚀容器复合材料衬里和复合材料。
CAS号：
性质：碳纤维制成的毡，简称碳毡。以聚丙烯腈基碳毡为例，定积重量500g/m2和1000g/m2，纵向和横向强度(N/mm2)各为0.12，0.16和0.10，0.12，断裂伸长各为3％、4％和18％、16％，电阻率(Ω·mm)各为4～6，3.5～5.5和7～9，6～8，导热系数各为0.06W/(m·K)(25℃)，比表面积均>1.5m2/g，灰分皆小于0.3％，含硫量皆<0.03％。制法有：(1)碳短丝气流成网后针刺；(2)预氧丝毡碳化；(3)聚丙烯腈纤维毡预氧化和碳化。用作真空炉和惰性气体炉绝热材料、热的气体或液体和熔融金属滤材、燃料电池多孔电极、催化剂载体、耐腐蚀容器复合材料衬里和复合材料。