1) in-situ forming techique
原位固化成型
2) consolidation in-situ forming
原位凝固成型
1.
A new consolidation in-situ forming process for high-performance aluminium oxide ceramic using starch as the consolidator/binder was investigated.
为获得以淀粉作凝固剂原位凝固成型氧化铝高性能陶瓷的方法,文中探讨了酯化淀粉添加量对陶瓷浆料流变特性以及成型出的素坯的线收缩、密度、干坯强度和显微结构的影响。
3) in-situ immobilization
原位固化
1.
The reaction condintions for in-situ immobilization of tannin in black wattle barks and adsorption characterization of in-situ immobilized black wattle barks(ISIB) to Fe3+ were investigated.
研究了黑荆树皮中单宁原位固化的反应条件及原位固化黑荆树皮(ISIB)对水溶液中Fe3+的吸附特性。
4) in-situ colloidal forming process
原位凝固胶态成型工艺
1.
The less viscous dense alumina suspensions were obtained for the effective application in the in-situ colloidal forming process.
制备了低粘度、高固相含量氧化铝悬浮浆料,并将其有效地应用于原位凝固胶态成型工艺中。
6) In-situ forming
原位成型
1.
Gelcasting is an in-situ forming process in which slurry of ceramic powder in a solution of organic monomer is cast.
Al_2O_3陶瓷凝胶注模成型是把传统陶瓷成型工艺与高分子化学反应相结合的一种崭新的陶瓷成型工艺，陶瓷凝胶注模过程是一种原位成型过程，它主要是利用陶瓷浆料中的有机单体在一定条件下发生聚合反应，使陶瓷浆料凝胶固化成型。
补充资料：金属基复合材料原位生长成型
金属基复合材料原位生长成型
in- situ fabrication of metal matrix composites
金属基复合材料原位生长成型动一sl’tu fabrica·tion of metal matrix eomposites金属在一定组成和环境条件下，局部形成增强体与原金属构成的复合材料。例如，定向凝固使参与共晶反应的a和刀两相同时从液相中以棒状或层状规则排列生长。另外，如有包晶或偏晶反应的两相合金，或成分偏离共晶成分，也能通过定向凝固使两相规则排列生长，但工艺条件苛刻。 原位生长成型必须满足3个条件:①有温度梯度的加热方式;②满足平面凝固条件;③两相的成核和生长要协调进行。二元系共晶材料的平面凝固条件为立、月丛丝鱿‘旦立V一Z人式中认为液相温度梯度，V为凝固速度，mL为液相线斜率，Q为共晶成分，Co为合金成分，及为原溶质在液相中的扩散系数。 在定向凝固设备上要求有很大的认。目前原位生长成型有功率降低法(民约30℃/cm)、快速凝固法(位约100℃/cm)、液态金属冷却法(仅约300℃/cm)、流态床急冷法(GL约300℃/cm)和区域熔化液态金属冷却法(q约1200℃/cm)。后者制备大直径试棒尚有困难，一般采用快速凝固法，因为它设备简单，操作方便，不受液态金属的污染。(胡壮麒)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。