1) Concentrated Sulphuric Acid Corrosion
浓硫酸腐蚀
2) Resistance to Concentrated Sulfuric Acid Corrosion
耐浓硫酸腐蚀
4) sulfate resistance
硫酸盐腐蚀
1.
Research methods:The performances of concrete with the anticorrosive mixture were investigated in the experiments, such as concrete chloride diffusivity, sulfate resistance and drying/wetting cycle in corrosive environments, etc.
研究方法:通过混凝土离子渗透性试验、硫酸盐腐蚀试验、干湿腐蚀循环试验等对耐腐蚀辅料的性能进行了测试,并对该耐腐蚀混凝土辅料的耐腐蚀机理进行了分析。
5) sulfate attack
硫酸盐腐蚀
1.
Constitutive relation of sulfate attacked concrete under uniaxial compression;
硫酸盐腐蚀后混凝土单轴受压本构关系
2.
Thaumasite form of sulfate attack in the concrete of Yong an dam;
新疆永安坝混凝土的碳硫硅钙石型硫酸盐腐蚀
6) sulfate corrosion
硫酸盐腐蚀
1.
Study on the sulfate corrosion of concrete under the action of loading;
荷载作用下的混凝土硫酸盐腐蚀研究
2.
A novel method was presented to improve the sulfate corrosion resistance of concrete with surface treatment by super-absorbent resin (SAR) synthesized in situ, i.
硫酸盐腐蚀是导致混凝土耐久性劣化的一个重要因素。
3.
At present, the research of concrete durability is an important part of the research of concrete structures; both concrete carbonization and sulfate corrosion are important parts of the concrete durability.
混凝土耐久性研究是当今混凝土结构研究中的一个重要组成部分,而混凝土碳化与硫酸盐腐蚀均是混凝土耐久性研究的重要组成部分。
补充资料：盐浓差电池腐蚀
分子式：
CAS号：
性质：同一金属的不同部位所接触的介质的盐浓度不同，形成盐浓差电池而导致的腐蚀。通常，电池中与较稀溶液接触的部分，因其电极电位较负，成为电池的阳极遭到腐蚀。而与较浓溶液接触部分，由于其电极电位校正，成为电池的阴极，溶液中的金属离子可在此析出。
CAS号：
性质：同一金属的不同部位所接触的介质的盐浓度不同，形成盐浓差电池而导致的腐蚀。通常，电池中与较稀溶液接触的部分，因其电极电位较负，成为电池的阳极遭到腐蚀。而与较浓溶液接触部分，由于其电极电位校正，成为电池的阴极，溶液中的金属离子可在此析出。