1) explosive leakage
爆漏
1.
Based on the explosive leakage conditions of power plant boiler "four tubes" in central china electric power corporation,we make a summarization,analyze the cause,and bring forward the measures and advices of avoiding it happening.
总结华中区域28个电厂火电机组1998-2002年锅炉受热面管爆漏情况,分析爆漏原因,提出防止锅炉受热面管爆漏的措施和建议。
2.
In order to improving the safety and economy of boilers and reducing the potential casualties and loss of property,the causations of superheater\'s explosive leakage were statistically analyzed from 100 accidents which were vended in literature.
以100余起公开报道的锅炉过热器爆漏事故案例进行统计分析为基础,将引起过热器爆漏的直接原因归纳为长期超温、短期超温、腐蚀、磨损和焊接缺陷,对产生事故的机理和主要原因进行了探讨和归类,认为运行管理不当是造成过热器爆漏的最重要方面。
2) bursting leakage
爆漏
1.
The causes of bursting leakage of "four tubes" in boiler are analyzed.
对神头第一发电厂捷制锅炉“四管”爆漏的原因进行了分析 ,针对造成爆漏的主要原因提出了相应的对
3) leakage
[英]['li:kɪdʒ] [美]['likɪdʒ]
爆漏
1.
The burst-leakage of "four tube kinds" in utility boilers are main causes leading to non-planned boiler shutdown in power plants,while the main causes resulting in burst-leakage of "four tube kinds" in boilers are:overtemperature excess heating,corrosion,worn-out,and thermal fatigue etc.
电站锅炉"四管"爆漏事故是造成电厂非计划停炉的主要原因,而超温过热、腐蚀、磨损、热疲劳等是造成锅炉"四管"爆漏的主要原因。
2.
The leakage of boiler heating surface accident seriously disserves the normal operation of plant,results in great economic losses.
锅炉受热面爆漏的发生,一直影响着火力发电厂的正常运行,造成巨大的经济损失,分析了水冷壁、过热器、再热器和省煤器爆漏原因,并对常见的爆管问题提出了相应的防范措施。
3.
In the paper,the frequency of boiler tube leakage is counted up in Zhangjiakou Power Plant since the first units gone into operation,the reason of the faults are analyzed,the countermeasures to prevent tubes leakage are introduced,and the esperience in these work is affirmed to make use for reference.
通过总结张家口发电厂第一台机组投产以来锅炉“四管”爆漏发生的次数、原因,分析了在防止锅炉爆管方面采取的措施,肯定了目前取得的成绩,以供借鉴。
4) explosion
[英][ɪk'spləʊʒn] [美][ɪk'sploʒən]
爆漏
1.
The causes of explosion are fatigue failure due to resonant vibration.
湖南益阳电厂#2炉后水冷壁延伸拉稀管在机组试运调试阶段发生爆漏。
2.
The reasons of boiler tubes explosion were analyzed.
分析了锅炉四管爆漏事故产生的原因，提出了预防措施及监测手段，并介绍了国内外应用现状和关键技术。
5) burst and leakage
爆漏
1.
The analysis and precaution of boiler four pipes burst and leakage;
锅炉四管爆漏分析及预防
2.
Directing against the problems of water-wall tube burst and leakage in seal-water tank for a 2100 t/h boiler in one thermal power plant, the cause analysis has been carried out through several means, such as macroscopic examination, chemical composition analysis, mechanical performance analysis, and metallurgical structure analysis etc.
针对某火电厂 2 10 0t/h锅炉水封槽部位水冷壁管爆漏问题 ,通过宏观检验 ,化学成分、力学性能及金相组织分析等手段对其原因进行了分析 ,认为该爆管属于应力拉裂所致。
6) blasting crater
爆破漏斗
1.
The formation of a normal blasting crater for the break blasting of a roadway in rock with high residual stress was investigated based on the theory of cylindrical blasting crater.
以柱装药爆破漏斗理论为基础,对高地应力巷道崩落爆破标准漏斗形成进行研究,导出了高应力条件下形成崩落爆破标准漏斗的判断准则,进而导出了相应条件的巷道崩落爆破参数计算式。
2.
The blasting crater curves of two different charges,the relationship between blasting crater volume and charge embedment depth and crater radius,the optimum blasting crater embedment depth,the critical blasting crater embedment depth and the unit consumption of explosives were disc.
根据利文斯顿爆破能量平衡准则,在安庆铜矿生产现场,进行了系列单孔爆破漏斗试验以及变孔距多孔同段爆破漏斗试验。
补充资料：爆破漏斗
爆破漏斗
blasting crater
匕00PO IOudou爆破漏斗(blasting erater)药包在岩石中爆破后，在自由面形成的凹坑。爆破漏斗是工程爆破中计算装药量和爆破体积的依据，按照爆破作用性质的不同，将爆破漏斗分为标准抛掷爆破漏斗、加强抛掷爆破漏斗和减弱抛掷爆破漏斗(见爆破作用指数)。构成爆破漏斗的要素有:最小抵抗线W;爆破漏斗半径;;爆破作用半径R;爆破漏斗深度D;爆破漏斗可见深度h和漏斗张开角(破裂角)0(见图)。蚀之 爆破漏斗图
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条