1) tetragonal perovskite structure
四方钙钛矿结构
1.
It was found that the tetragonal perovskite structure formed at 900 ℃ and the lattice parameters kept nearly the same as those of not doping with SmVO4.
XRD谱图显示,在900℃下处理的样品形成了单相稳定的四方钙钛矿结构晶体,其晶格常数比没有进行掺杂的SmVO4晶格常数略微降低,说明Sr已经很好地掺杂进入SmVO4的晶格结构中;在650~750℃,单电池最大输出功率密度为209。
2) perovskite structure
钙钛矿结构
1.
XRD PATTERN CHARACTER OF SrTiO_3-based perovskite structure;
SrTiO_3基钙钛矿结构X射线衍射谱特征
2.
2) powders with an orthogonal perovskite structure were prepared using the sol-gel method.
XRD图谱表明Nd1-xZnxFeO3粉体为正交钙钛矿结构,产物为纳米级颗粒(16~17。
3.
6)all have orthorhombic perovskite structure.
研究表明:合成的系列纳米材料均具有正交钙钛矿结构,Mn的掺杂对材料La0。
3) perovskite
[pə'rɔvz,kait]
钙钛矿结构
1.
Colossal magnetoresistance effect in the perovskite-type La_(0.9)Sb_(0.1)MnO_3 material;
钙钛矿结构La_(0.9)Sb_(0.1)MnO_3的庞磁电阻性质
2.
Study on Preparations and Magnetic Properties of Manganites with Perovskite Structure;
钙钛矿结构锰氧化物的合成及性质研究
3.
The LaNiO_3 samples with perovskite structure were prepared using citric acid aqueous solution, then heated at high temperature in air.
利用柠檬酸盐分解法,在空气气氛中高温烧结,合成了钙钛矿结构的LaNiO3。
4) Perovskite Type Structure
钙钛矿结构
1.
The effects of composition and crystal lattice of lead-free ceramics with perovskite type structure, which is employed in dielectric capacitor applications, have been widely investigated.
本文以具有钙钛矿结构的无铅电容器陶瓷材料[BaTiO_3、Bax(Bi_(0。
6) hexagonal perovskite
六方类钙钛矿结构
补充资料：钙钛矿型铁氧体
分子式：
CAS号：
性质：又称钙钛矿型铁氧体。具有钙钛矿型结构的铁氧体。其化学式为AFeO3(式中A为Y或一部分其他稀土元素)。其晶体结构与天然钙钛石(CaTiO3)相同，属正交晶系。具有单轴各向异性。饱和磁化强度很低，约为(4.9～11.4)×10-4T，其泡径(磁泡处于稳定状态时的直径)较大，迁移率较低。用它制作的磁泡存储器具有非挥发性、抗辐射能力强。利用薄膜技术可实现集成化，在密度与半导体存储器相同情况下功耗约可低2～3个数量级。主要用作磁泡材料。
CAS号：
性质：又称钙钛矿型铁氧体。具有钙钛矿型结构的铁氧体。其化学式为AFeO3(式中A为Y或一部分其他稀土元素)。其晶体结构与天然钙钛石(CaTiO3)相同，属正交晶系。具有单轴各向异性。饱和磁化强度很低，约为(4.9～11.4)×10-4T，其泡径(磁泡处于稳定状态时的直径)较大，迁移率较低。用它制作的磁泡存储器具有非挥发性、抗辐射能力强。利用薄膜技术可实现集成化，在密度与半导体存储器相同情况下功耗约可低2～3个数量级。主要用作磁泡材料。